Anatomical Structures and Fiber Quality of Four Lesser-Used Wood Species Grown in Indonesia
( Sari Delviana MARBUN ),( Imam WAHYUDI ),( Jajang SURYANA ),( Deded Sarip NAWAWI ) 한국목재공학회 2019 목재공학 Vol.47 No.5
This study aimed to investigate the anatomical structure and fiber quality of four lesser-used wood species namely Benuang (O. sumatrana), Duabanga (D. moluccana), Pisang Merah (H. hellwigii), and Terap (A. odoratissimus). This study evaluated its suitability for raw material in pulp and paper manufacturing. The anatomical structure was observed macro- and microscopically. Macroscopic structures were observed directly to the wood samples, while microscopic characteristics were observed through microtome specimens. Fiber dimension was measured through macerated specimens and fiber quality was analyzed following the Rachman and Siagian’s method. Results showed that these four timber species have similarity in the indistinct growth ring, diffuse porous in a radial pattern, rounded solitary vessel outline, 1 to 3 cells of ray width, deposits within the rays, fiber length, and cell wall thickness. Differences were found on vessel diameter, vessel grouping, vessel frequency, tyloses existence, type of axial parenchyma, and ray height. Based on fiber length and its derived values, the wood fibers of all species studied are suitable for pulp and paper manufacturing. They belong to the II quality class. The produced pulp and paper would have good quality, especially in tensile, folding, and tear strength. To promote their utilization, silviculture aspect of these four species has to be well understood.
( Sarah Augustina ),( Sari Delviana Marbun ),( Sudarmanto ),( Narto ),( Deazy Rachmi Trisatya ),( Eko Budi Santoso ),( Dhimas Pramadani ),( Nanda Nur Afni ),( Tushliha Ayyuni Fariha ),( Gabriel Wiwind 한국목재공학회 2023 목재공학 Vol.51 No.6
Samama wood (Anthocephalus macrophyllus (Roxb) Havil) is a fast-growing and lesser-utilized wood species that has inferior properties; therefore, its quality needs to be improved. This research aimed to determine the effect of citric acid impregnation at high curing temperatures on the dimensional stability and mechanical properties of wood. Citric acid solution with 10% concentration (w/w) was impregnated into wood samples by vacuum-pressure method (-0.5 cmHg, 30 min; 0.7 MPa, 3 h), followed by curing process at 140℃, 160℃, and 180℃ of temperature for 1 h. In comparison, the other wood samples were heat treated at the same temperatures and time. The results showed that the increase in curing and heat temperatures for both treatments were directly proportional to the dimensional stability, but inversely proportional to the mechanical properties. Citric acid impregnated had higher density, dimensional stability, and mechanical properties, except for modulus of rupture, than that of heat treatment. The optimum temperature is suggested at 160℃ in both treatments.