Evaluation on Spalling Properties of Specimen Size with PP Fiber and Fireproof Coating
Kim, Gyu-Yong,Min, Choong-Siek,Lee, Tae-Gyu,Miyauchi, Hiroyuki,Park, Gyu-Yeon,Lee, Gwang-Jun The Korean Institute of Building Construction 2011 한국건축시공학회지 Vol.11 No.4
High Strength Concrete (HSC) has weakness that in a fire, it is spalled and brittles. The phenomenon of spalling is made by water vapor's being confined in watertight concrete. This study is aimed to evaluate explosive spalling properties of high strength concrete with ${\square}100{\times}100{\times}200$ mm specimen and ${\square}400{\times}400{\times}1500$ mm column. To prevent spalling of concrete, fireproof coating and PP fiber are used. As a result, ${\square}400{\times}400{\times}1500$ mm column was prevented spalling likes ${\times}100{\times}100{\times}200$ mm specimen. When concrete protected failure to explosive spalling, quantity heat ratio (which fireproof coating specimen to pp fiber mixed specimen) between ${\square}100{\times}100{\times}200$ mm and ${\square}400{\times}400{\times}1500$ mm was maximum value at 20 minute, but difference of quantity heat ratio decreased and quantity heat ratio of each specimen is almost same at 30 minute.
Kim, Yong-Ro,Lee, Jae-Hyun,Min, Choong-Siek,Park, Jong-Ho The Korean Institute of Building Construction 2014 한국건축시공학회지 Vol.14 No.1
This research examined the effect of the quality of aggregate on concrete workability and compressive strength through an investigation into regional aggregate used in domestic ready mixed concrete plants. Through the research, it was found that aggregate for ready mixed concrete shows poor quality overall. The main factor of deterioration in the quality of the concrete is the particle size of fine aggregate and fine particle content in coarse aggregate. The quality of aggregate significantly influences concrete's workability, which is defined based on 0.08mm passage related with powder and absorption. In addition, poor aggregate quality leads to increased water content in concrete to secure workability, which is related with a decline in the compressive strength and durability of concrete.