방전 플라즈마 소결법의 공정특성이 Ni분말 소결체에 미치는 영향
김기엽(Gi-Yeob Kim) 산업기술교육훈련학회 2013 산업기술연구논문지 (JITR) Vol.18 No.3
The spark plasma sintering(SPS) process, that enables rapid sintering under the condition of lower temperature combined with pressure application in various environment, is proposed as a novel process of powder forming. The effects of various sintering conditions on the density of Ni powder compacts were investigated by observing the densification behavior and actual temperature of specimens, and the results are summarized as follows: The densification rate of powder compacts was very fast in spite of shorter process time(less than 10 min) compare to conventional sintering process. The relative density of sintered compact was 98 % when the powder compact was sintered at 800 ℃ for 1 min under 40 MPa pressure. The densification behavior was affected by heating rate of powder compacts, shape and size of raw powder. At 800 ℃ of die temperature, the temperature of specimen inside was 920 ℃.
-
-
3.6wt%C-2.5wt%Si 오스템퍼드 구상흑연주철의 프로세싱 윈도우에 미치는 열처리 및 구리 첨가의 영향
권도영,오정혁,김기엽,권해욱,Kwon, Do-Young,Oh, Jeong-Hyeok,Kim, Gi-Yeob,Kwon, Hae-Wook 한국주조공학회 2021 한국주조공학회지 Vol.41 No.4
3.6wt%C-2.5wt%Si 구상흑연주철을 오스템퍼링 열처리하는 동안 프로세싱 윈도우에 미치는 오스템퍼링 온도, 오스테나이트화 처리 온도와 시간, 구리 첨거량 그리고 사전 열처리의 영향을 연구하였다. 350℃의 오스템퍼링 처리 온도에서 최대 프로세싱 윈도우를 얻었다. 프로세싱 윈도우는 오스테나이트화 처리 온도가 850에서 900℃로 증가함에 따라 증가하였으나 950℃로 증가하면 오히려 감소하였다. 프로세싱 윈도우는 오스테나이트화 처리 시간이 30분에서 2시간까지 증가함에 따라 증가하였다가 4시간일 때 감소하였다. 최적 오스템퍼링 처리 조건은 900℃에서 2시간인 것으로 나타났다. 프로세싱 윈도우는 구리 첨가량이 0.0~0.8wt% 범위에서 증가함에 따라 증가하였다. 프로세싱 윈도우는 주방 상태의 구상흑연주철에 비하여 사전 노르말라이징 처리로 증가하였으며 사정 어닐링 처리로 감소하였다. The effects of austempering temperature, austenitizing temperature and time, added copper content and prior heat-treatment on the processing window of 3.6wt%C-2.5wt%Si ductile cast iron during austempering. The maximum processing window was obtained at 350℃ of austempering temperature. The processing window was increased with increased austenitizing temperature from 850 to 900℃; however, it decreased at 950℃. The processing window was increased with increased austenitizing time from 0.5 to 2 hours and rather decreased for 4 hours. The optimum condition of austenitizing was obained at 900℃ for 2 hours. The processing window was increased with copper content added in the range of 0.0~0.8wt%. The processing window was increased by prior normalizing heat-treatment and decreased by prior annealing in comparison with that for the as-cast state,
-
-
Lateral growth of PEO films on Al7050 alloy in 0.1 M NaAlO₂
Sungmo Moon(문성모),Gi Yeob Kim(김기엽) 한국표면공학회 2021 한국표면공학회지 Vol.54 No.4
This paper investigated generation behavior of micro-arcs and growth behavior of PEO films on the AA7050 disc specimen in 0.1 M NaAlO₂ solution under the application of 1200 ㎐ anodic pulse current. Morphologies, thickness and surface roughness of PEO films were examined at the edge part and central part separately. Micro-arcs were generated first at the edge part and then moved towards the central part with PEO treatment time, indicating lateral growth of PEO films. The lateral growth resulted in uniform PEO thickness of about 5 ㎛ and surface roughness of about 0.5 ㎛. Moving of the arcs from the edge towards the central part appeared only one time and large size arcs were generated at the edge before completing the central part with small size micro-arcs. This suggests that vertical growth starts before completing the lateral growth. Large size arcs generated at the edge resulted in the formation of relatively large size pores within the PEO films on the AA7050 disc specimen.
-
W치환 2205 이상 스테인리스강의 크리프 특성 평가에 관한 연구
김기엽,최병호,남기우,안용식 한국비파괴검사학회 2004 한국비파괴검사학회지 Vol.24 No.1
22Cr-5Ni 2상 스테인리스강의 합금원소 중 몰리브덴(Mo) 원소를 텅스텐(W)으로 치환하여 크리프거동에 미치는 영향을 조사하였다. 크리프시험은 600℃와 650℃의 온도에서 실시하였다. 650℃ 크리프 시에는 취약한 금속간화합물인 σ상이 석출하였으며 이것은 크리프수명을 급격히 감소시키는 역할을 하였다. Mo에 대한 W원소의 치환은 일반적으로 σ상의 석출을 지연시킨다고 알려져 있으나, 2wt.%까지 W 치환을 실시한 본 연구범위에서는 크리프 수명 및 최소 크리프속도에 뚜렷한 영향을 미치지 못하였다. 크리프손상의 정도를 평가하기 위하여 크리프시편에 대한 초음파검사를 실시하였다. 크리프온도 600℃에서는 크리프시편의 수명이 증가함에 따라 음속이 비례적으로 증가하였으나 650℃에서는 반대로 감소하였다. The effect of the substitution of Tungsten(W) for Molybdenum(Mo) on the creep behaviour of 22Cr-5Ni duplex stainless steel(DSS) has been investigated. Creep tests were carried out at 600℃ and 650℃. Intermetallic σ phase is precipitated during creep at 650℃, at which creep rupture time was much lower compared with at 600℃. The substitution of W for MO in the duplex stainless steel was known to retard the formation of σ phase. Minimum creep rate and creep rupture time, however, were hardly influenced by the substitution of 2wt.% W. An ultrasonic measurement for the creep specimens has been carried out for the evaluation of creep damage. The sound velocity increases propotionally with the increase of creep rupture time at 600℃ of creep temperature. On the contrary, the sound velocity decreases with the increase of rupture time at 650℃, which can be correlated with the microstructural evolution during creep.