CuInGaSe<sub>2</sub> 태양전지용 Mo 후면 전극의 조직 및 전기광학적 특성
채수병,김명한,Chae, Su-Byung,Kim, Myung-Han 한국재료학회 2010 한국재료학회지 Vol.20 No.8
Mo thin films were used for the back electrode because of the low resistivity in the Mo/$CuInGaSe_2$ contact in chalcopyrite solar cells. $1\;{\mu}m$ thick Mo thin films were deposited on soda lime glass by varying the Ar pressure with the dc-magnetron sputtering process. The effects of the Ar pressure on the morphology of the Mo back electrode were studied and the relationships between the morphology and electro-optical properties, namely, the resistivity as well as the reflectance of the Mo thin films, were investigated. The resitivity increased from $24\;{\mu}{\Omega}{\cdot}cm$ to $11833\;{\mu}{\Omega}{\cdot}cm$; this was caused by the increased surface defect and low crystallinity as the Ar pressure increased from $3{\times}10^{-3}$ to $3{\times}10^{-2}\;Torr$. The surface morphologies of the Mo thin films changed from somewhat coarse fibrous structures to irregular and fine celled structures with increased surface cracks along the cell boundaries, as the Ar pressure increased from $3{\times}10^{-3}$ to $3{\times}10^{-2}\;Torr$. The changes of reflectances in the visible light range with Ar pressures were mainly attributed to the surface morphological changes of the Mo thin films. The reflectance in the visible light range showed the highest value of 45% at $3{\times}10^{-3}\;Torr$ and decreased to 18.5% at $3{\times}10^{-2}\;Torr$.
-
전해증착 Cu(In,Ga)Se<sub>2</sub> 태양전지 박막의 열처리 특성
채수병,신수정,최재하,김명한,Chae, Su-Byung,Shin, Su-Jung,Choi, Jae-Ha,Kim, Myung-Han 한국재료학회 2010 한국재료학회지 Vol.20 No.12
Cu(In,Ga)$Se_2$(CIGS) photovoltaic thin films were electrodeposited on Mo/glass substrates with an aqueous solution containing 2 mM $CuCl_2$, 8 mM $InCl_3$, 20 mM $GaCl_3$ and 8mM $H_2SeO_3$ at the electrodeposition potential of -0.6 to -1.0 V(SCE) and pH of 1.8. The best chemical composition of $Cu_{1.05}In_{0.8}Ga_{0.13}Se_2$ was found to be achieved at -0.7 V(SCE). The precursor Cu-In-Ga-Se films were annealed for crystallization to chalcopyrite structure at temperatures of 100-$500^{\circ}C$ under Ar gas atmosphere. The chemical compositions, microstructures, surface morphologies, and crystallographic structures of the annealed films were analyzed by EPMA, FE-SEM, AFM, and XRD, respectively. The precursor Cu-In-Ga-Se grains were grown sparsely on the Mo-back contact and also had very rough surfaces. However, after annealing treatment beginning at $200^{\circ}C$, the empty spaces between grains were removed and the grains showed well developed columnar shapes with smooth surfaces. The precursor Cu-In-Ga-Se films were also annealed at the temperature of $500^{\circ}C$ for 60 min under Se gas atmosphere to suppress the Se volatilization. The Se amount on the CIGS film after selenization annealing increased above the Se amount of the electrodeposited state and the $MoSe_2$ phase occurred, resulting from the diffusion of Se through the CIGS film and interaction with Mo back electrode. However, the selenization-annealed films showed higher crystallinity values than did the films annealed under Ar atmosphere with a chemical composition closer to that of the electrodeposited state.