손희식,홍석호,김문일 ( H . S . Sohn,S . H . Hong,M . I . Kim ) 한국열처리공학회 1994 熱處理工學會誌 Vol.7 No.2
The purpose of this study is to clarify the influence of the reaction temperature and AlCl₃content on the aluminide coating formation on Ni-based superalloy IN713C in CVD process and to compare its throwing power with that of Pack Cementation process. Aluminide coating was formed by CVD in hot-wall stainless tube reactor from an AlCl₃-H₂mixture in the temperature range 850∼1050℃. At reaction temperature 850℃, the coating thickness and the content of aluminium at the surface were increased as AlCl₃heating temperature was raised. At reaction temperature 1050℃, they were not influenced by the variation of AlCl₃heating temperature. When AlCl₃heating temperature was fixed 125℃, the phases of the coatings were varied from Ni₂Al₃to Al-rich NiAl and to Ni-rich NiAl with the reaction temperature. Therefore, in this stucy the reaction temperature has been found to be a major factor in determining the phase formed in CVD process. The throwing power of CVD was superior to that of Pack Cementation.