수크로스 함유 분무용액으로부터 분무열분해 공정에 의한 미세 Ba-Nd-Ti-O 분말 합성 = Synthesis of Fine Ba-Nd-Ti-O Powders by Spray Pyrolysis from Spray Solution with Sucrose

다국어 초록 (Multilingual Abstract)

Nano-sized $BaNd_2Ti_5O_{14}$ powders were prepared by the spray pyrolysis process. Sucrose used as the organic additive enabled the formation of nano-sized $BaNd_2Ti_5O_{14}$ powders. The powders prepared from the spray solution without sucrose had a spherical shape, dense structure and micron size before and after calcination. However, the precursor powders prepared from the spray solution with sucrose had a large size, and hollow and porous morphology. The precursor powders had an amorphous crystal structure because of the short residence time of the powders inside the hot wall reactor. The complete decomposition of sucrose did not occur inside the hot wall reactor. Therefore, the precursor powders obtained from the spray solution with sucrose of 0.5M had a carbon content of 39.2wt.%. The powders obtained from the spray solution with sucrose of 0.5M had a slightly aggregated structure of nano-sized primary powders of $BaNd_2Ti_5O_{14}$ crystalline phase after calcination at $1000^{\circ}C$. The calcined powders turned into nano-sized $BaNd_2Ti_5O_{14}$ powders after milling. The mean size of the $BaNd_2Ti_5O_{14}$ powders was 125 nm.

참고문헌 (Reference)

1 A. Ioachim, 109 : 183-, 2004

2 D. Y. Kim, 417 : 254-, 2006

3 C. H. Lu, 98 : 33-, 2003

4 Y. P. Fu, 31 : 667-, 2005

5 B. H. Jung, 25 : 3187-, 2005

6 R. Ratheesh, 211 : 1-, 1998

7 H. Zheng, 27 : 4479-, 2007

8 O. Dernovsek, 21 : 1693-, 2001

9 I. S. Cho, 30 : 1181-, 2004

10 Y. Xu, 83 : 2893-, 2000

11 S. W. Kwon, 27 : 247-, 2007

12 V. Vinothini, 32 : 99-, 2006

13 L. Guo, 60 : 3011-, 2006

14 H. Xu, 58 : 1582-, 2004

15 Z. Peng, 66 : 102-, 2003

16 K. K. Lee, 395 : 280-, 2005

17 Y. Itoh, 17 : 3222-, 2002

18 Y. N. Ko, 36 : 63-, 2010

19 김동은, "BaO-B2O3-SiO2-K2O-xTiO2 Glass의 첨가에 의한 BaNd2Ti5O14-Glass 복합체의 마이크로파 유전특성" 한국세라믹학회 44 (44): 110-115, 2007