The h-BN powder was synthesized by amorphous B₂O₃ and activated carbon at 1550℃ in nitrogen atmosphere, whose properties were examined according to MgB6 addition. Amount of MgB6 addition was varied in the range of 0~10 wt% of the initial mixture...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A104294966
2009
Korean
KCI등재,SCOPUS,SCIE
학술저널
53-57(5쪽)
0
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
The h-BN powder was synthesized by amorphous B₂O₃ and activated carbon at 1550℃ in nitrogen atmosphere, whose properties were examined according to MgB6 addition. Amount of MgB6 addition was varied in the range of 0~10 wt% of the initial mixture...
The h-BN powder was synthesized by amorphous B₂O₃ and activated carbon at 1550℃ in nitrogen atmosphere, whose properties
were examined according to MgB6 addition. Amount of MgB6 addition was varied in the range of 0~10 wt% of the initial mixture.
It was observed that MgB6 addition led to an increase in the amount and the grain size of h-BN and decrease in the amount of B₄C
forming. When MgB6 added 5 wt%, the amount and crystallinity of h-BN increased as the holding time at the synthesis temperature
was prolonged. It was also confirmed that the regularity of three-dimensional ordering of h-BN increases.
다국어 초록 (Multilingual Abstract)
The h-BN powder was synthesized by amorphous B₂O₃ and activated carbon at 1550℃ in nitrogen atmosphere, whose properties were examined according to MgB6 addition. Amount of MgB6 addition was varied in the range of 0~10 wt% of the initial mixtur...
The h-BN powder was synthesized by amorphous B₂O₃ and activated carbon at 1550℃ in nitrogen atmosphere, whose properties
were examined according to MgB6 addition. Amount of MgB6 addition was varied in the range of 0~10 wt% of the initial mixture.
It was observed that MgB6 addition led to an increase in the amount and the grain size of h-BN and decrease in the amount of B₄C
forming. When MgB6 added 5 wt%, the amount and crystallinity of h-BN increased as the holding time at the synthesis temperature
was prolonged. It was also confirmed that the regularity of three-dimensional ordering of h-BN increases.
참고문헌 (Reference)
1 H. Lorenz, "of the Initial Crystallinity on the High Pressure-High Temperature Phase Transition in Boron Nitride" 52 : 1909-1916, 2004
2 Joon S. J., "Vapour-Phase Reduction and the Synthesis of Boron-Based Ceramic Phases" 30 : 607-614, 1995
3 Kempfer L., "The Many Faces of Boron Nitride" 107 : 41-44, 1990
4 Aydo˘gdu A., "Formation of Boron Nitride" 23 : 3153-3161, 2003
5 Hasan Erdem Çamurlu, "Effect of Calcium Carbonate Addition on Carbothermic Formation of Hexagonal Boron Nitride" 28 (28): 679-689, 2008
6 Hwang Chyi Ching, "Combustion Synthesis of Boron Nitride Powder" 13 (13): 680-686, 1998
7 T. S. Bartniskaya, "Catalytic Synthesis of Graphite-like Boron Nitride" 35 (35): 296-300, 1996
1 H. Lorenz, "of the Initial Crystallinity on the High Pressure-High Temperature Phase Transition in Boron Nitride" 52 : 1909-1916, 2004
2 Joon S. J., "Vapour-Phase Reduction and the Synthesis of Boron-Based Ceramic Phases" 30 : 607-614, 1995
3 Kempfer L., "The Many Faces of Boron Nitride" 107 : 41-44, 1990
4 Aydo˘gdu A., "Formation of Boron Nitride" 23 : 3153-3161, 2003
5 Hasan Erdem Çamurlu, "Effect of Calcium Carbonate Addition on Carbothermic Formation of Hexagonal Boron Nitride" 28 (28): 679-689, 2008
6 Hwang Chyi Ching, "Combustion Synthesis of Boron Nitride Powder" 13 (13): 680-686, 1998
7 T. S. Bartniskaya, "Catalytic Synthesis of Graphite-like Boron Nitride" 35 (35): 296-300, 1996
마이크로에멀젼법을 이용한 나노 CoFe₂O₄ 분말의 실리카 코팅
20 nm 두께의 ITO층이 코팅된 ITO/PET Sheet의 저항 및 균열형성 특성 연구
중공형 미세구를 이용한 마이크로셀룰라 지르코니아의 기공 특성 고찰
학술지 이력
연월일 | 이력구분 | 이력상세 | 등재구분 |
---|---|---|---|
2023 | 평가예정 | 해외DB학술지평가 신청대상 (해외등재 학술지 평가) | |
2020-01-01 | 평가 | 등재학술지 유지 (해외등재 학술지 평가) | |
2010-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2008-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2006-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2004-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2001-01-01 | 평가 | 등재학술지 선정 (등재후보2차) | |
1998-07-01 | 평가 | 등재후보학술지 선정 (신규평가) |
학술지 인용정보
기준연도 | WOS-KCI 통합IF(2년) | KCIF(2년) | KCIF(3년) |
---|---|---|---|
2016 | 0.16 | 0.16 | 0.17 |
KCIF(4년) | KCIF(5년) | 중심성지수(3년) | 즉시성지수 |
0.16 | 0.16 | 0.331 | 0.06 |