Tm³+과 Nd³+ 이온이 도핑된 유리세라믹의 형광특성과 에너지 전달 = Photoluminscence and Energy Transfer in Tm³+ and Nd³+ Co-doped Glass Ceramics

다국어 초록 (Multilingual Abstract)

We synthesized oxyfluoride glass-ceramics containing CaF₂nanocrystals doped with Tm³+ and Nd³+ ions and conducted a spectroscopic investigation of the energy transfer between doped ions. The emission intensity was improved in the glass ceramics due to the CaF₂ nanocrystals. Energy transfers between Tm³+ ions and from Tm³+ to Nd³+ ions were investigated by exciting Tm³+-doped and Tm³+/Nd³+-codoped glass ceramics at 470 nm and by using excitation spectra and time-resolved photoluminescence of Tm$^{\mathrm{3+}}$ ions at 650 nm and Nd³+ ions at 670 nm. We also confirmed the energy transfer from the ^{3}H_{4} level of Tm^{3+} ions to the ^{4}F_{5/2} level of Nd³+ ions in the emission spectrum.

국문 초록 (Abstract)

산소불화 유리에 Tm³+이온과 Nd³+이온을 도핑하고 적절한 열처리를 통해 CaF³+ 결정이 내부에 형성된 유리세라믹을 제조하고 도핑이온들의 에너지 전달과정을 분광분석을 통해 조사하였다 CaF³+ 나노 결정으로 인해 형광효율이 현저하게 향상하였다 470 nm 에서 여기하여 Tm³+이온과 Tm이온간의 에너지 전달과 Tm³+이온으로부터 Nd³+이온으로의 에너지 전달을 650 nm에서의 Tm^{3+} 이온 형광과670 nm 에서의 Nd³+이온의 형광의 여기 스펙트럼과 시분해 형광스펙트럼 분석을 통해 연구하였다 또한 형광스펙트럼 분석을 통해 Tm이온의 ^{3}H_{4} 준위로부터 Nd³+이온의 ^{4}F_{5/2}준위로의 에너지전달의 존재를 확인하였다.

참고문헌 (Reference)

1 J. J. Eilers, 96 : 151106-, 2010

2 M. Inokuti, 43 : 1978-, 1965

3 F. Auzel, 104 : 139-, 2004

4 J. Li, 113 : 223507-, 2013

5 F. Lahoz, 120 : 6180-, 2004

6 M. J. Dejneka, 239 : 149-, 1998

7 P. Babu, 19 : 1836-, 2011

8 Y. Katayama, 33 : 176-, 2010

9 F. Lahoz, 90 : 201117-, 2007

10 X. Y. Sun, 621 : 322-, 2010

11 F. Lahoz, 281 : 3691-, 2008

12 G. Lakshminarayana, 404 : 3348-, 2009

13 G. Lakshminarayana, 355 : 2668-, 2009

14 R. Reisfeld, "Lasers and Excited States of Rare-Earth" Springer-Verlag 157-198, 1977

15 A. A. Kaminskii, "Laser Crystals" Springer-Verlag 166-318, 1990