카본아미노실리카 블랙 고성능감수제(CASB-SP)를 사용한 블랙콘크리트의 Mock-up Test 및 현장적용 = Mock up test and Field Application of Black Concrete Applying Superplasticizer containing Carbon Amino Silica Black

다국어 초록 (Multilingual Abstract)

This paper presents the result of a mock-up test and field application of concrete that is black in color thanks to theapplication of superplasticizer containing carbon amino silica black (CASB-SP). Mock-up specimen with a size of3000×1500×40 mm was fabricated with black concrete applying 0.5% of CSAB-SP with 27 MPa. After dividing thezone in wall mock-up specimen, three different water repelling agents were applied to verify its effect of efflorescenceprevention. It was found that the use of CASB-SP with 0.5% made the black concrete develop a highly clear blackcolor, and the epoxy type water repelling agent had better performance in efflorescence prevention. Based on mock-uptest, field application was conducted with bridge member. It was also found that the application of CASB-SP showedfavorable results in black color development.

국문 초록 (Abstract)

최근에는 생활수준 향상으로 인간친화적인 공간창조 등의장적인 측면에서 다양한 요구가 나타나고 있다. 본 연구에서는 무주태권도원의 2개의 블랙콘크리트 교량에 기존연구에서 얻어진 카본아미노실리카블랙 고성능 감수제(CASB-SP)를 적용하기 위한 Mock up test와 현장적용사항에 대하여 보고하고자 하였다. Mock up test 결과 일반적인 품질 항목은 양호하게 나타났고, 백화방지와 관련한발수제 도포는 에폭시계가 가장 양호한 것으로 나타나 현장적용에 활용하였다. 현장적용 결과 역시 기초적 특성은 모두 양호 하였고, 검정색 색상구현도 양호하였는데, 기존의카본블랙 분말 색소를 이용하는 경우보다 시공성, 품질 모두 양호하면서 30 % 정도의 저렴한 경제성도 확인할 수 있었다.

참고문헌 (Reference)

1 류현기, "카본블랙을 혼화재료로 사용한 콘크리트의 특성 분석" 한국건축시공학회 10 (10): 59-66, 2010

2 한천구, "CASB의 혼입율 변화에 따른 광물질 혼화재 치환 초고강도 시멘트 페이스트의 특성분석" 대한건축학회 27 (27): 105-112, 2011

3 Han CG, "Analysis of the Effect of Superplasticizer combined CASB on Ultra High Strength Mortar and Concrete Using Mineral Admixture" 6 (6): 72-79, 2011

4 Han JS, "An Improvement Method on the Using Problem of the Ground Granulate Blast-Furnace Slag as a Concrete Admixture in Ready-Mixed Concrete Plant" 15 (15): 6-7, 2003