보로실리케이트 유리의 이온교환에 의한 고강도 투명방탄소재의 제조 = Fabrication of High Strength Transparent Bulletproof Materials by Ion Exchanged Borosilicate Glass

다국어 초록 (Multilingual Abstract)

Borosilicate glass (81% $SiO_2$-2% $Al_2O_3$-13% $B_2O_3$-4% $Na_2O_3$) was prepared, and the glass was ion exchanged in $KNO_3$ powder containing different temperature and time. The $K^+-Na^+$ ion exchange takes place at the glass surface and creates compressed stress, which raise the mechanical strength of the glass. The depth profile of $Na^+$ and $K^+$ was observed by electron probe micro analyzer. With the increasing heat-treatment time from 0min to 20min, the depth profile was increased from 17.1um to 29.4um, but mechanical properties were decreased. It was also found out that excessive heat treatment brings stress relaxation. The Vickers hardness, Fracture Toughness and bending strength of ion exchanged samples at $570^{\circ}C$ for 10min were $821.8H_v$, $1.3404MPa{\cdot}m^{1/2}$, and 953MPa, which is about 120%, 180%, and 450% higher than parent borosilicate glass, respectively. Transmittance was analyzed by UV-VIS-NIR spectrophotometer. Transmittance of ion exchanged borosilicate glass was decreased slightly at visible-range. It can be expected that transparent bulletproof materials in more light-weight and thinner by ion exchanged borosilicate glass.

참고문헌 (Reference)

1 김태윤, "방탄소재 활용을 위한 SLS 유리의 이온교환 효과" 한국군사과학기술학회 13 (13): 114-119, 2010

2 K. K. Mallick, "Strengthening of Container Glasses by Ion-exchange Dip Coating" 351 : 2524-2536, 2005

3 H. E. Yunqiu, "Mechanical Strength Improvement of Glass by Ion Exchange in the Solid State" 80 : 283-291, 1986

4 A. G. Evans, "Fracture Toughness Determination by Indentation" 59 (59): 371-372, 1976

5 B. R. Lawn, "Elastic/Plastic Indentation Damage in Ceramics" 63 (63): 574-581, 1980

6 D. J. Green, "Compressive Surface Stress in Glass : An Old Curiosity" 92 : 1059-1063, 1999

7 V. P. Pukh, "Atomic Structure and Strength of Inorganic Glasses" 47 (47): 876-881, 2005