Laser 용접한 스테인리스강의 용접부위의 부식특성에 관한 평가

다국어 초록 (Multilingual Abstract)

Laser welding was carried out on austenitic 304 (STS 304) and 2 APU stainless steels. In this case, the differences between the corrosion caracteristics of th welding zones of the two stainless steels were investigated using electrochemical methods. The Vickers hardness values of the weld metal (WM) zones in both cases, the STS 304 and 22 APU stainless steels, showed relatively higher values than those of other welding zones. The corrosion current densities of the heat affected zone (HAZ) of the 22 APU and the base metal (BM) zone of the STS 304 exhibited the highest values compared to the other welding zones. It is generally accepted that whe STS 304 stainless steel is welded using a general welding method, intergranular corrosion is often observed at the grain boundary because of its chromium depletion area. However, when laser welding was performed on both the STS 304 and 22 APU stainless steels, no intergranular corrosion was observed at any of the welding zones. Consequently, it is considered that the intergranular corrosion of stainless steel can be controlled with the application of laser welding.

목차 (Table of Contents)

• ABSTRACT
• 1. 서론
• 2. 사용 재료 및 실험 방법
• 3. 실험결과 및 고찰
• 4. 결론
• 참고문헌

참고문헌 (Reference)

1 김복인, "피복성분에 의한 수중용접봉의 아크 안정성 개선에 관한 연구" 15 (15): 75-79, 2001

2 김종도, "펄스 Nd:YAG 레이저를 이용한 모터용 스테이터 적층코어의 용접특성 [Ⅰ]- 레이저 용접성에 미치는 가공변수의 영향 -" 한국마린엔지니어링학회 30 (30): 629-635, 2006

3 안석환, "용접열사이클 재현에 의한 SS400강 및 STS304강의 특성 평가- 제1보: 기계적 특성 및 조직" 한국해양공학회 19 (19): 64-71, 2005

4 김민남, "습식수중 용접봉의 기계적 성질에 관한 연구" 14 (14): 56-61, 2000

5 오종인, "선체구조용 A급 강재의 하이브리드 용접에 대한 열 및 역학적 특성에 관한 연구" 한국해양공학회 21 (21): 64-68, 2007

6 김진경, "선박용 디젤기관의 주철부품 보수용접 특성에 관한 연구" 한국해양공학회 20 (20): 41-45, 2006

7 전대희, "부식과 방식의 관리" 일중사 294-298, 1985

8 김종도, "리튬이온전지의 밀봉용접을 위한 펄스 Nd:YAG레이저 용접조건의 최적화" 한국마린엔지니어링학회 30 (30): 623-628, 2006

9 신민교, "기계공작법" 아성출판사 242-245, 1987

10 이학렬, "금속부식공학" 연경문화사 246-247, 1991

11 Devine, T. M., "The Mechanism of Sensitization of Austenitic Stainless Steel" 30 (30): 135-, 1990

12 Hiroshi, I., "Study of Weld Decay in SUS 304" 47 (47): 153-, 1978

13 Bilmes, P.D., "Microstructure and Pitting Corrosion of 13CrNiMo Weld Metal" 48 : 3261-3270, 2006

14 Raja, V.S., "Influence of Nitrogen on the Pitting Corrosion Behaviorof 904L Weld Clad" 40 (40): 1609-1625, 1998

15 Tsay, L.W., "Hydrogen Sulphide Stress Corrosion Cracking of 2.25Cr-Mo Steel Weldments" 39 (39): 1165-1176, 1997

16 Nobuo, F., "Effect of Thermal Cycles on Corrosion Resistance in a Type 304 Stainless Steel" 33 (33): 55-, 1964

17 I.H.Lo, "Effect of Heat Treatment on the Pitting Corrosion Behavior of 347 SS Weld Overlay" 한국부식방식학회 31 (31): 361-367, 2002

18 Lee, Y.H., "Crevice Corrosion Resistance of Stainless Steel in Natural Sea Water with Different Post Welding Treatment" 2 (2): 219-224, 2003

19 Yoshihiko, M., "Corrosion of Austenitic Stainless Steel Welds" 41 (41): 154-, 1972

20 장석기, "Al 7075의 마찰교반 용접부 특성에 관한 연구" 한국마린엔지니어링학회 30 (30): 30-41, 2006

21 Kyung-ManMoon, "A Study on the Post-Weld Heat Treatment Effect to Mechanical Properties and Hydrogen Embrittlement for Heating Affected Zone of a RE 36 Steel" 한국부식방식학회 32 (32): 283-288, 2003