Investigation of lauric acid dopant as a novel carbon source in MgB₂ wire

다국어 초록 (Multilingual Abstract)

We fabricated lauric acid (LA) doped MgB<SUB>2</SUB> wires and investigated the effects of the LA doping. For the fabrication of the LA-doped MgB<SUB>2</SUB> wires, B powder was mixed with LA at 0-5wt.% of the total amount of MgB<SUB>2</SUB> using an organic solvent, dried, and then the LA-treated B and Mg powders were mixed stoichiometrically. The powder mixture was loaded into an Fe tube and the assemblage was drawn and sintered at 900<SUP>o</SUP>C for 3h under an argon atmosphere. We observed that the LA doping induced the substitution of C for the B sites in MgB<SUB>2</SUB> and that the actual content of C increased monotonically with increasing LA doping level. The LA-doped MgB<SUB>2</SUB> wires exhibited a lower critical temperature (T<SUB>c</SUB>), but better critical current density (J<SUB>c</SUB>) behavior in a high magnetic field: the 5wt.% LA-doped sample had a J<SUB>c</SUB> value of 5.32x10<SUP>3</SUP>A/cm<SUP>2</SUP>, which was 2.17 times higher than that of the pristine sample (2.45x10<SUP>3</SUP>A/cm<SUP>2</SUP>) at 5K and 6T, suggesting that LA is an effective C dopant in MgB<SUB>2</SUB> for enhancing the high-field J<SUB>c</SUB> performance.