Al-Si 합금의 양극산화거동 및 규소화합물 제어 = Anodizing Behavior and Silicides Control in Al-Si Alloy System

다국어 초록 (Multilingual Abstract)

The anodic oxidation behavior of Si-containing aluminum alloy for diecasting was investigated. Especially, the property changes during anodization both on aluminum 1050 and 9 weight percentage silicon containing aluminum (Al-9Si) alloys were analyzed by the static current test. In order to fabricate a uniform anodic oxidation film by effect of Al-Si compound, nitric acid containing hydrofluoric acid had been used as a desmutter for aluminum alloy after alkaline etching. It was found that the level of voltage of Al-9Si alloy during the static current test was almost as double as higher than aluminum 1050 through anodization. By adding hydrofluoric acid in the nitric acid electrolyte, the silicon compound on the surface was removed, and the optimum amount of added hydrofluoric acid could be derived. It was also observed that the size of silicon compound formed on the surface could be refined by heat treatment at 500oC and followed water quenching.

참고문헌 (Reference)

1 L. Wang, 494 : 211-, 2006

2 J. He, 471 : 395-, 2009

3 L. E. Fratila-Apachitei, 49 : 1127-, 2004

4 J. -H. Lee, Seoul University 1976

5 B. Zhu, Jonkoping University 2017

6 K. -T. Kim, 24 (24): 179-, 1991

7 L. E. Fratila-Apachitei, 49 : 3169-, 2004

8 A. Forn, 202 : 1139-, 2007

9 L. E. Fratila-Apachitei, 200 : 5343-, 2006

10 H. -Y. Kim, Hanyang University 2010

11 J. -W. Moon, 23 (23): 34-, 1990

12 C. Blanc, 40 : 1019-, 1998

13 문성모, "주조용 Al-Si-Cu 알루미늄 합금의 기계가공 및 주조된 표면에서의 양극산화피막 형성" 한국표면공학회 42 (42): 260-266, 2009

14 전성일, "실험조건에 따른 알루미늄 다이캐스팅 소재의 양극산화 결과" 사단법인 인문사회과학기술융합학회 5 (5): 771-778, 2015