Si/SiC 혼합물의 소결특성에 미치는 첨가제의 영향 = Additive Effects on Sintering of Si/SiC Mixtures

다국어 초록 (Multilingual Abstract)

The effects of clay, aluminum hydroxide, and carbon powder on the sintering of a Si/SiC mixture from photovoltaic silicon-wafer production were investigated. Sintering temperature was fixed at $1,350^{\circ}C$ and the sintered bodies were characterized by SEM and XRD to analyze the microstructure and to measure the apparent porosity, absorptivity, and apparent density. The XRD peak intensity of SiC in the sintered body was increased by adding 5% carbon to the Si/SiC mixture. From this result, it is confirmed that Si in the Si/SiC mixture had reacted with the added carbon. Addition of aluminum hydroxide decreased the cristobalite phase and increased the stable mullite phase. The measurement of the physical properties indicates that adding carbon to the Si/SiC mixture enables us to obtain a dense sintered body that has high apparent density and low absorptivity. The sintered body produced from the Si/SiC mixture with aluminum hydroxide and carbon powder as sintering additives can be applied to diesel particulate filters or to heat storage materials, etc., since it possesses high thermal conductivity, and anticorrosion and antioxidation properties.

참고문헌 (Reference)

1 W. T. Kwon, 724 : 49-, 2012

2 U. Setiowati, 80 (80): 757-, 1997

3 V. M. Kevorkijan, 27 : 2705-, 1992

4 S. K. Lee, 29 : 5321-, 1994

5 A. Palermo, 177 : 259-, 1998

6 M. A. Mulla, 70 : 439-, 1991

7 F. J. Klug, 70 (70): 750-, 1987

8 S. Prochazka, 58 (58): 72-, 1975

9 N. Altinkok, 34 : 577-, 2003

10 S. Elomari, 30 : 3037-, 1995

11 정은진, "태양전지 産業에서 排出되는 Si waste로부터 SiC 분말 제조에 관한 硏究" 한국자원리싸이클링학회 19 (19): 44-49, 2010

12 윤기석, "SHS법을 이용한 복합분말(Al2O3-SiC) 제조시 TiO2첨가의 영향" 한국재료학회 12 (12): 48-53, 2002