유기발포제에 따른 적층형 PTC(Positive Temperature Coefficient of Resistance) 써미스터의 전기적 특성 = Electric Properties of the Laminate Type PTC(Positive Temperature Coefficient of Resistance) Thermistor According to Polymer Blowing Agent

다국어 초록 (Multilingual Abstract)

The electrical properties of a laminated SMD type PTC thermistor for microcircuit protection were investigated as a function of polymer blowing agent addition. Green ceramics for multilayered $BaTiO_3$-based PTCRs were formed by doctor blade method of barium titanate powders; we successfully laminated the sintered ceramic chips to obtain 10 layer chip PTCRs with PTC effect. The sintered density increases with increasing sintering temperature. The electrical properties of the sintered samples were strongly dependent on the calcination and addition of a polymer blowing agent. When $BaTiO_3$ powders containing 0.2 mol% of $Y_2O_3$ were calcined at $1000^{\circ}C$ for 2 hrs, the resistivity jump was of 1-2 orders of magnitude. The resistivity at room temperature increases according to the polymer blowing agent addition. Also, the sample using the calcined powder showed a lower resistivity than that of the sample prepared using powders without calcinations. With an increase in the OBSH, the magnitude of the resistivity jumped as a function of the temperature increase. The resistivity of the sintered bodies after the addition of 0.5 wt% polymer blowing agent at $1290^{\circ}C$ for 2 h was shown to be about $8.5{\Omega}{\cdot}cm$; the jump order of the sintered bodies was shown to be on the order of $10^2$.

참고문헌 (Reference)

1 M. Valant, 26 : 2777-, 2006

2 J. M. Haussonne, 66 (66): 801-, 1983

3 J. Qi, 116 : 215-, 2004

4 D. A. Tolino, 68 (68): C-292-, 1985

5 J. -G. Kim, 60 : 1505-, 2006

6 M. Kuwabara, 64 : C-170-, 1981

7 J. G. Kim, 77 : 255-, 2000

8 H. J. Kwon, 1 (1): 67-, 1992

9 I. C. Ho, 75 (75): 728-, 1992

10 S. K. Jo, 46 (46): 1076-, 2007

11 H. M. Al-Allak, 20 (20): 1645-, 1987

12 V. Shut, 43 (43): 5251-, 2008

13 이미재, "초소형 회로보호용 적층 PTC 써미스터의 출발원료 및 Sr 첨가에 따른 전기적 특성" 한국세라믹학회 48 (48): 525-530, 2011

14 정용근, "Sm을 첨가한 BaTiO₃계의 재산화 온도 및 시간에 따른 PTC 특성 변화" 한국세라믹학회 46 (46): 330-335, 2009