기계적합금화에 의한 $AC4A/SiC_p$복합재료의 제조 및 기계적 특성 = Fabrication and mdchanical properties of $AC4A/SiC_p$ composites by mechanical alloying

다국어 초록 (Multilingual Abstract)

Utilizing Mechanical Alloy Process, that were obt,ained the results from investigated formation process of AC4A/$SiC_p$. composite material powders and mechanical properties of their extrusion materials. The obtained results are as follow conclusions. AC4A-lOwt.% $SiC_p$ powders which were mechanically alloyed at 150rpm for 420min have been obtained finely and uniformly rounded powder particals that were reached the steady state which was saturated micro hardness about tlv 230 in the range size of 1 0 ~ 2 0$\mu \textrm{m}$. EDAX analysis tests have been resulted in a little amount of I'e conrents increasing with MA times, the artifical aging of AC4A/S$SiC_p$ composite materials was obtained the hardness with solution treated at $525^{\circ}C$ for lOhrs the maximum value of Hv 230 with aging at. $170^{\circ}C$ for 1000min. The Intensity and width of X-ray diffraction pattern were decreasing and widening because of grain boundary refinement and heterogeneous strain during mechanical alloying. Tensile tests at room temperature were carried out the maximum value of 37 Kgf/$\mu \textrm{mm}^2$ with ext,rused materials, 27 Kgf/$\mu \textrm{mm}^2$ with heat treated them at $500^{\circ}C$.