Experimental-Numerical Analysis of Bending Behavior of Reinforced Concrete Beam with Electrochemical Chloride Extraction-Strengthening

다국어 초록 (Multilingual Abstract)

The magnesium phosphate cement (MPC)-carbon fiber reinforced plastics (CFRP) strengtheningand electrochemical chloride extraction (ECE) integration experiment was carried out for reinforced concrete beams corroded by sodium chloride. Then the bending performance of the reinforced concrete beams was analyzed by test and numerical simulation. The reinforced concrete beams of the control group were energized to accelerate corrosion until the theoretical corrosion rate of the steel bars reached 10%. The second group of the beams were strengthened, and the other three groups of the beams were strengthened and the inside chloride was removed by electrochemistry method with different dechlorination current densities. The bending test results showed that the bending bearing capacity of the strengthenedconcrete beam increased by 18.22%. The bending bearing capacity of the strengthened and dechlorinated beam increased by 15.11%, 13.25% and 9.76%, respectively. The chloride ion content at the interface between steel bar and concrete reduced by 68.68% − 82.64%. In addition, the numerical simulation method of "standard cube test block-central pull out test block-reinforced concrete beam" was proposed. A 3D mesoscopic finite element plastic damage model of the reinforced concrete beams strengthened by MPC-CFRP was established. The numerical results were in good agreement with the experimental results.

참고문헌 (Reference)

1 Liu QF, "Three-phase modelling of electrochemical chloride removal from corroded steel-reinforced concrete" 70 : 410-427, 2014

2 Scrivener KL, "The interfacial transition zone(ITZ)between cement paste and aggregate in concrete" 12 (12): 411-421, 2004

3 "Standard for test method of concrete structures. GB 50152-2012"

4 "Standard for quality control of concrete. GB 50164-2011"

5 Li YY, "Research on reinforced concrete beam enlarged cross section method experiment and finite element simulation" 638-640 : 208-213, 2014

6 Li Y, "Research of electrochemical chloride extraction and reinforcement of concrete column using MPC-bonded carbon fiber reinforced plastic sheet & mesh" 153 : 436-444, 2017

7 Karpate H, "Repair and rehabilitation of corrosiondamaged concrete elements using FRP composite wraps" 8 (8): 147-150, 2011

8 Choi HT, "Partially bonded near-surfacemounted CFRP bars for strengthened concrete T-beams" 25 (25): 2441-2449, 2011

9 Firmo JP, "Numerical simulation of the fire behaviour of thermally insulated reinforced concrete beams strengthened with EBR-CFRP strips" 126 : 360-370, 2015

10 Mondal P, "Nanotechnology in construction 3" Springer 2009

11 Huang YJ, "Monte Carlo simulations of meso-scale dynamic compressive behavior of concrete based on x-ray computed tomography images" 97 : 102-115, 2016

12 Shengqiang Ma, "Models Reviewed for Predicting CFRP Shear Contribution of Strengthened Reinforced Concrete Box Beam" 대한토목학회 23 (23): 3644-3659, 2019

13 "Method of testing cements - Determination of strength. GB/T 17671-1999"

14 Peng YJ, "Mesoscopic numerical simulation of fracture process and failure mechanism of concrete based on convex aggregate model" 2019 : 2019

15 Song ZH, "Mesoscopic analysis of concrete under excessively high strain rate compression and implications on interpretation of test data" 46 : 41-55, 2012

16 Wriggers P, "Mesoscale models for concrete : Homogenisation and damage behaviour" 42 (42): 623-636, 2006

17 Kim SM, "Meso-scale computational modeling of the plastic-damage response of cementitious composites" 41 (41): 339-358, 2011

18 Malumbela G, "Load-bearing capacity of corroded, patched and FRP-repaired RC beams" 63 (63): 797-812, 2011

19 Miranda JM, "Limitations and advantages of electrochemical chloride removal in corroded reinforced concrete structures" 37 (37): 596-603, 2007

20 Rahman MM, "Innovative hybrid bonding method for strengthening reinforced concrete beam in flexure" 79 : 370-378, 2015

21 Altin S, "Improving shear capacity of existing RC beams using external bonding of steel plates" 27 (27): 781-791, 2005

22 Grondin F, "How to consider the Interfacial Transition Zones in the finite element modelling of concrete?" 58 : 67-75, 2014

23 Song L, "Fatigue performance of corroded reinforced concrete beams strengthened with CFRP sheets" 90 : 99-109, 2015

24 Al-Hammoud R, "Fatigue flexural behavior of corroded reinforced concrete beams repaired with CFRP sheets" 15 (15): 42-51, 2011

25 Saraswathy V, "Extraction of chloride from chloride contaminated concrete through electrochemical method using different anodes" 158 : 549-562, 2018

26 Li Y, "Experimental-computational approach to investigate compressive strength of magnesium phosphate cement with nanoindentation and finite element analysis" 190 : 414-426, 2018

27 Li Y, "Experimental study on the effect of different dispersed degrees carbon nanotubes on the modification of magnesium phosphate cement" 200 : 240-247, 2019

28 Xie JH, "Experimental study on rehabilitation of corrosiondamaged reinforced concrete beams with carbon fiber reinforced polymer" 38 : 708-716, 2013

29 Gao RX, "Experimental study on flexural performance of reinforced concrete beams subjected to different plate strengthening" 176 : 565-581, 2017

30 Jin L, "Experimental and numerical investigations on the size effect of moderate high-strength reinforced concrete columns under small-eccentric compression" 27 (27): 657-685, 2018

31 Zong-Xing Zhang, "Experimental and Theoretical Investigation on Flexural Behavior of Corroded Steel Beams Strengthened by CFRP Plate" 대한토목학회 24 (24): 2160-2172, 2020

32 Yue Li, "Experimental Study on Reinforcement and Chloride Extraction of Concrete Column with MPC-CFRP Composite Anode" 대한토목학회 23 (23): 1766-1775, 2019

33 Polder RB, "Electrochemical chloride removal from concrete prisms containing chloride penetrated from sea water" 10 (10): 83-88, 1996

34 Orellan JC, "Electrochemical chloride extraction : Efficiency and side effects" 34 (34): 227-234, 2004

35 Jin L, "Effect of cross-section size on the flexural failure behavior of RC cantilever beams under low cyclic and monotonic lateral loadings" 156 : 567-586, 2018

36 Ormellese M, "Corrosion inhibitors for chlorides induced corrosion in reinforced concrete structures" 36 (36): 536-547, 2006

37 El Maaddawy T, "Carbon-fiber-reinforced polymer repair to extend service life of corroded reinforced concrete beams" 9 (9): 187-194, 2005

38 Rafi MM, "Aspects of behaviour of CFRP reinforced concrete beams in bending" 22 (22): 277-285, 2008

39 Lin H, "A study on the deterioration of interfacial bonding properties of chloride-contaminated reinforced concrete after electrochemical chloride extraction treatment" 197 : 228-240, 2019

40 Jin L, "A combined experimental and numerical analysis on the seismic behavior of short reinforced concrete columns with different structural sizes and axial compression ratios" 27 (27): 1416-1447, 2018

41 Zhou RX, "3D mesoscale finite element modelling of concrete" 192 : 96-113, 2017