물유리의 수분 함량 및 열처리 온도에 따른 다공체의 특성 = Characteristics of Porous Ceramics Depending on Water Content of the Water Glass and Heat Treatment Temperature

다국어 초록 (Multilingual Abstract)

Porous ceramics which have closes pore were fabricated by heat treatment at 100$\∼$ 600$^{\circ}C$ for 30 min using dried water glasses with 25, 35, and 45 wt$\%$ water contents. Size and distribution of the closed pore were varied depending on the water contents and heat treatment temperature. The expansion procedure could be distinguished by two stages. The frist stage occurred around loo$\%$ due to the evaporation of water and the second stage occurred at 200$\∼$400$^{\circ}C$ due to the decomposition of Si-OH compounds. The specimen was not expanded successfully because of the softening of the dried water glass at 500$\∼$600$^{\circ}C$.

참고문헌 (Reference)

1 "T. Aono and Y. Matsuda" soc. chemical eng. japan 25 (soc. chemical eng. japan 25): 126-132, 1999

2 "Processing of Porous Ceramics." 1674-1680, 1992

3 "Processing and Properties of Cellular silica synthesized by Foaming Sol-Gels" 85-92, 1990

4 "Preparation for Porous Inorganic Materials by Foaming Slurry." 1280-1288, 1998

5 "Preparation for Porous Ceramics Using Low Grade Clay 35" 575-582, 1998

6 "H. Nakao and H. Katsuki" soc. chemical eng. japan 12 (soc. chemical eng. japan 12): 286-, 1993

7 "Glass science & engineering" 1996.

8 "Fracture Behavior of Open-Cell Ceramics" 1145-1152, 1989

9 "Experimental Study on Foaming Ability and Foam Stability of Surfactant Aqueous Solution" 230-236, 1995

10 "Effects of Fabrication Variables and Microstructures on the Compressive strength of open Cell Ceram. Soc. 36" 954-961, 1999