Synthesis of 4-arms hydroxy-functionalized PMMA-b-PE through combining free radical polymerization with coordination polymerization

다국어 초록 (Multilingual Abstract)

The copolymerization of MMA with ethylene was promoted by metallocene complex in the presence ofinitiator tetra(2,3-epoxy propoxy)silane (Is), reducing agent Zn and cocatalyst MAO, combining freeradical polymerization with coordination polymerization via sequential monomer addition strategy inone-pot to produce 4-arms hydroxy-functionalized PMMA-b-PE. The effects of polymerizationconditions such as temperature, time, ethylene pressure and Al/Ti molar ratio on the polymerizationperformance were investigated. 4-Arms hydroxy-functionalized PMMA-b-PE was obtained by solventextraction and determined by GPC, MALLS, DSC, FT-IR, WAXD and 1H(13C) NMR. The DSC result indicatedthat the 4-arms hydroxy-functionalized PMMA-b-PE had one Tg at 87.0 ℃ and one Tm at 117.0 ℃ whichattributed to Tg of PMMA segment and Tm of PE segment, respectively. The microstructure of 4-armshydroxy-functionalized PMMA-b-PE was further confirmed by WAXD, FT-IR, and 13C NMR analysis.
These results demonstrated that the obtained 4-arms block copolymer consisted of PMMA segment andcrystalline PE segment.

참고문헌 (Reference)

1 Y. Cai, 37 : 9728-, 2004

2 Y. Luo, 126 : 13910-, 2004

3 H. Gao, 129 : 11828-, 2007

4 Y. Zhao, 127 : 14158-, 2005

5 T. Shibata, 128 : 7497-, 2006

6 K. Zhang, 42 : 2313-, 2009

7 A. D. Asandei, 126 : 15932-, 2004

8 A. D. Asandei, 39 : 7549-, 2006

9 A. D. Asandei, 44 : 1106-, 2006

10 L. Ma, 3171-, 2011

11 H. Wang, 4 : 423-, 2010

12 Y. Cai, 38 : 271-, 2005

13 H. Zhang, 127 : 9364-, 2005

14 Q. Huang, 47 : 767-, 2006

15 Y. Kong, 51 : 3859-, 2010

16 L. Ma, 48 (48): 4-, 2010

17 L. Ma, 46 (46): 33-, 2008

18 X. Zhang, 50 : 2068-, 2012

19 L. Ma, 7 : 689-, 2009

20 Y. Sheng, 2 : 179-, 2008

21 Aaltonen, 31 : 79-, 1995

22 Q. Huang, 39 : 4068-, 2001

23 Q. Huang, 50 : 45-, 2001

24 Q. Huang, 41 : 2909-, 2005

25 L. Oliva, 17 : 745-, 1996

26 G.L. Ricardo, 419-, 2007

27 L. Izzo, 200 : 1086-, 1999

28 Zhi Liu, "Synthesis of (co-)polyethylene with broad molecular weight distribution by the heterogenous Ziegler–Natta catalysts via one-pot strategy" 한국공업화학회 18 (18): 2217-2224, 2012

29 "Catalyst system: CpTiCl3/Zn/Is/MMA = 8/12/1/300; monomer: MMA (3 mL); radical polymerization of MMA was carried out at 90 8C for 2.5 h in 1,4-dioxane (IE = 0.68, Mn = 0.27 104, MWD = 1.51). When the experiment was performed in a 300 mL glass Schlenk, the mixture color was changed into lime-green, demonstrating the formation of metallocene complex radical CpTi(III)Cl2"