MgFe2O4 formation, grain growth in Fe2O3, Fe solid-solution limit in MgO for MgO-Fe2O3 mixture were studied by means of investigating the distribution of phases and compositions in reaction area between MgO and Fe2O3. The reaction area at equlibrium w...
MgFe2O4 formation, grain growth in Fe2O3, Fe solid-solution limit in MgO for MgO-Fe2O3 mixture were studied by means of investigating the distribution of phases and compositions in reaction area between MgO and Fe2O3. The reaction area at equlibrium was composed with MgO-FexO matrix and MgFe2O4 precipitation, MgFe2O4 was formed by precipitating from MgO-FexO matrix dependent on oxygen partial pressure. Fe contents was exponentially decreased with diffusion distance in MgO single crystal, and thus Fe solid-solution limitation in MgO was about 4mol%. The grain growth rate in Fe2O3 base was increased with Mg contents diffused from MgO single crystal.