YBCO 초전도 선재를 이용한 단일 브릿지 및 이중 브릿지 형태로의 변형에 따른 국소적 영역에서의 물리적 특성 비교 분석 = Spatially-resolved Analysis of the Superconducting Properties in a YBCO-coated Conductor with Striation - A Comparative Study -

다국어 초록 (Multilingual Abstract)

Measuring and visualizing the local transition critical temperature and critical current density of a YBCO-coated conductor, rather than just a rough average value, through a nondestructive way is significant. In particular, in this study, we transformed the shape of a sample with striation and compared a single-bridge-type sample with a two-bridge-type sample. The samples were examined under a low-temperature scanning-laser Hall-probe microscope (LTSLHPM) at temperatures near the transition temperature. The result showed no differences in the superconducting properties within the margin of error. Thus, the ac loss is expected to be reduced by patterning the sample.

국문 초록 (Abstract)

본 연구에서는 기하학적인 구조의 변형이 미시적 영역에서의 물리적특성에 미치는 영향을 분석하기 위해 YBCO 초전도 선재 시료를 단일브릿지 형태와 단일 브릿지를 평행하게 배열한 이중 브릿지의 형태로제작하였다. 액체질소를 주입한 저온의 진공 용기 내에서 저온 주사레이저 및 홀 소자 현미경을 이용하여 국소적인 영역에서의 임계온도 및전류밀도를 측정하여 시료의 형태에 따라 어떻게 달라지는 가를 보았다.
그 결과 단일 브릿지와 이중 브릿지의 국소적 영역에서의 초전도 특성은실험 오차범위 내에서 차이가 없었으며, 특히 단일브릿지 형태의 GdBCO 시료와 비교하여 보았을 때 차이가 극명하게 드러남을 알 수 있었다.
따라서 시료를 패터닝 함으로써 초전도 특성에 손실 없이 교류 손실을저감할 수 있을 것으로 기대된다.

참고문헌 (Reference)

1 G. W. Crabtree, 36 : 4021-, 1987

2 L. J. Swartzendruber, 64 : 483-, 1990

3 C. P. Bean, 8 : 250-, 1962

4 C. P. Bean, 36 : 31-, 1964

5 S. K. Park, 51 : 241-, 2011

6 J. Mcdonald, 53 : 8643-, 1996

7 E. H. Brandt, 48 : 12893-, 1933

8 R. Gross, 57 : 651-, 1994

9 T. H. Johansen, 54 : 16264-, 1996

10 E, Zeldov, 49 : 9802-, 1994