AlGaAs/GaAs HBT 응용을 위한 Pd/Si/Pd/Ti/Au 오믹 접촉 = Pd/Si/Pd/Ti/Au Ohmic Contact for Application to AIGaAs/GaAs HBT

다국어 초록 (Multilingual Abstract)

Pd/Si/Pd/Ti/Au ohmic contact to n-type InGaAs was investigated with rapid thermal annealing conditions. Minimum specific contact resistivity of $3.9\times10^{-7}\Omega\textrm{cm}^2$ was achieved at $400^{\circ}C$/20sec. This was related to the formation of Pd-Si compounds by rapid thermal annealing and the in-diffusion of Si atoms to InGaAs surface. However, the specific contact resistivity increased slightly to low-$10^{-6}\Omega \textrm{cm}^2$ at $400^{\circ}C$ for longer than 30 seconds, and to high-$10^{-7}$ at 425~$450^{\circ}C$ for 10 seconds. This resulted from the formation of Pd-Ga compounds. Superior ohmic contact and non-spiking planar interface between ohmic materials and InGaAs were maintained after annealing at high temperature. Therefore, this thermally stable ohmic contact system is a promising candidate for compound semiconductor devices.