MgO-$SnO_2$계 Spinel 채요에 대한 NiO, $TiO_2$의 영향 = Influence of NiO, $TiO_2$ for MgO-$SnO_2$ System Spinel Pigment

다국어 초록 (Multilingual Abstract)

To observe the influence of tetrahedral and octahedral preference of cations of Ni2+, Ti4+ upon the formation and the color development of the MgO-SnO2 spinel containing Ni2+ and Ti4+ ions, the gradual substitution of Ni2+ ions for Mg2+ ions and of Ti4+ ions for Sn4+ ions of the spinel in NiO-MgO-SnO2-TiO2 system was carried out. On samples prepared by calcining the oxide and basic carbonate mixtures at 130$0^{\circ}C$ for 1.5 hour, the X-ray analysis, measurement of reflectance and the test of their stability as a glaze pigment were also carried out. On samples prepared by calcining the oxide and basic carbonate mixtures at 130$0^{\circ}C$ for 1.5 hour, the X-ray analysis, measurement of reflectance and the test of their stabiality as a glaze pigment were also carried out. The results are summarized as follows. 1) As increasing the amounts of Ni2+ ions in the xNiO.(2-x)MgO.SnO2 system, spinel was not formed easily, and the mixed-spinel was formed in NiO.MgO.SnO2 of x=1 but the spinels was not formed completely in the range of x>1.5 2) The spinels was not more formed in NiO-MgO-TiO2 system than NiO-MgO-SnO2 system. Therefore, Ti4+ ions have strong octahedral preference than Sn4+ ions. The color changed the yellow region little. The mixed-spinel or non-spinel was formed easily NiO.TiO2, MgO.TiO2 of illmenite type as the gradual substitution of Ti4+ ions for Sn4+ ions. 3) The results of glaze test. The color changed from white through graish brown to brown as the gradual substitution of Ni2+ ions for Mg2+ ions in calcium-zinc glaze and calcium glaze, and from white through light yellowish beige to dull beige in tile glaze. Also, the color did not change generally as the gradual substitution of Ti4+ ions for Sn4+ ions in NiO-MgO-SnO2-TiO2 system.