Sulfonated amine-poly(ether sulfone)s (S-APES)s were prepared by nitration, reduction and sulfonation of poly(ether sulfone) (ultrason<SUP>(</SUP>R)-S6010). Poly(ether sulfone) was reacted with ammonium nitrate and trifluoroacetic anhydrid...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107585879
Seo, D.W. ; Lim, Y.D. ; Lee, S.H. ; Jeong, Y.G. ; Hong, T.W. ; Kim, W.G.
2010
-
SCI,SCIE,SCOPUS
학술저널
13088-13095(8쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
Sulfonated amine-poly(ether sulfone)s (S-APES)s were prepared by nitration, reduction and sulfonation of poly(ether sulfone) (ultrason<SUP>(</SUP>R)-S6010). Poly(ether sulfone) was reacted with ammonium nitrate and trifluoroacetic anhydrid...
Sulfonated amine-poly(ether sulfone)s (S-APES)s were prepared by nitration, reduction and sulfonation of poly(ether sulfone) (ultrason<SUP>(</SUP>R)-S6010). Poly(ether sulfone) was reacted with ammonium nitrate and trifluoroacetic anhydride to produce the nitrated poly(ether sulfone), and was followed by reduction using tin(II)chloride and sodium iodide as reducing agents to give the amino-poly(ether sulfone). The S-APES was obtained by reaction of 1,3-propanesultone and the amino-poly(ether sulfone) (NH<SUB>2</SUB>-PES) with sodium methoxide. The different degrees of nitration and reduction of poly(ether sulfone) were successfully synthesized by an optimized process. The reduction of nitro group to amino was done quantitatively, and this controlled the contents of the sulfonic acid group. The films were converted from salt to acid forms with dilute hydrochloric acid. Different contents of sulfonated unit of the S-APES were studied by FT-IR, <SUP>1</SUP>H NMR spectroscopy, differential scanning calorimetry (DSC), and thermo gravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion exchange capacity (IEC), a measure of proton conductivity, was evaluated. The S-APES membranes exhibit conductivities (25 <SUP>o</SUP>C) from 1.05 x 10<SUP>-3</SUP> to 4.83 x 10<SUP>-3</SUP> S/cm, water swell from 30.25 to 66.50%, IEC from 0.38 to 0.82 meq/g, and methanol diffusion coefficients from 3.10 x 10<SUP>-7</SUP> to 4.82 x 10<SUP>-7</SUP> cm<SUP>2</SUP>/S at 25 <SUP>o</SUP>C.
Hydrogen storage behaviors of platinum-supported multi-walled carbon nanotubes
Hydrogen permeation on Al2O3-based nickel/cobalt composite membranes