To obtain fundamental informations for fine tungsten carbide powders, the preparation of fine tungsten carbide by vapor phase reaction of WCl_6-CCl₄-H₂ system has been carried out in the temperature range of 800-1300℃. The effects of reaction co...
To obtain fundamental informations for fine tungsten carbide powders, the preparation of fine tungsten carbide by vapor phase reaction of WCl_6-CCl₄-H₂ system has been carried out in the temperature range of 800-1300℃. The effects of reaction conditions on particle size and morphology of tungsten carbide powders have been investigated by utilizing X-ray diffraction, SEM and TEM techniques. The content of WC increased remarkably with increasing the reaction temperature and the maximum content was about 97% at 1100℃ in the condition of the flow rate of Ar gas 200㎖/min, H₂ gas 100㎖/min and CCl₄ gas 40㎖/min. The particle size of the reation products obtained at 1100℃ was about 0.05㎛ and the shape of WC was spherical. The particle size decreased linearly with increasing reation temperature. Also the crystallite size increased gradually with increasing reaction temperature.
Ti3Al-Nb 합금의 α2 상의 형상과 부피분율이 기계적 성질에 미치는 영향
철욕식 용융환원로에서 용융산화철 환원반응의 속도론적 모델링
Rene 95 의 열간정수압 성형과 후열처리가 전입자경계구조 특성에 미치는 영향