PEMFC에서 막 열화가 전극 열화에 미치는 영향 = Effect of Membrane Degradation on the Electrode Degradation in PEMFC

다국어 초록 (Multilingual Abstract)

The membrane and electrode were degraded coincidentally at real PEMFC(Proton Exchange Membrane Fuel Cells) operation condition. But the interaction membrane degradation between electrode degradation has not been studied. The effect of membrane degradation on electrode degradation was studied in this work. We compared electrode degradation after membrane degradation and electrode degradation without membrane degradation. I-V performance, hydrogen crossover current, impedance and TEM were measured after and before degradation of MEA. Membrane degradation enhanced hydrogen crossover, and then Pt particle growth rate was reduced. Increase of hydrogen crossover by membrane degradation reduced the electrode degradation rate.

참고문헌 (Reference)

1 Zhai, Y., "The stability of Pt/ C Catalyst in H3PO4/PBI PEMFC During High Temperature Life Test" 164 : 126-133, 2006

2 Williams, M. C., "The U. S. Department of Energy, Office of Fossil Energy Stationary Fuel cell Program" 143 (143): 191-196, 2005

3 Wilson, M. S., "Surface Area Loss of Supported Platinum in Polymer Electrolyte Fuel Cells" 140 : 2872-2877, 1993

4 Ho Lee, "Pinhole formation in PEMFC membrane after electrochemical degradation and wet/dry cycling test" 한국화학공학회 28 (28): 487-491, 2011

5 박권필, "PEMFC에서 전극 열화가 전해질 막 열화에 미치는 영향" 한국화학공학회 51 (51): 68-72, 2013

6 Pozio, A., "Nafion Degradation in PEFCs from End Plate Iron Contamination" 48 : 1543-1548, 2003

7 Wilkinson, D. P., "Handbook of Fuel Cell: Fundamentals Technology and Applications, Vol. 3" John Wiley & Sons Ltd. 611-612, 2003

8 Xie, J., "Durability of PEFCs at High Humidity Conditions" 152 : 104-113, 2005

9 Guilminot, E., "Detection of Ptz+ ions and Pt Nanoparticles Inside the Membrane of a Used PEMFC" 154 : 96-105, 2007

10 Luo, Z., "Degradation Behavior of Membrane-electrode-assembly Materials in 10-cell PEMFC Stack" 31 : 1838-1854, 2006

11 Akita, T., "Analytical TEM Study of Pt Particle Deposition in the Proton-exchange Membrane of a Membrane- electrode-assembly" 159 : 461-467, 2006

12 Knights, S. D., "Aging Mechanism and lifetime of PEFC and DMFC" 127 : 127-134, 2004

13 Curtin, D. E., "Advanced Materials of Improved PEMFC Performance and Life" 131 : 41-48, 2004

14 Curtin, D., "Advanced Materials for Improved PEMFC Performance and Life" 131 : 41-48, 2004

15 Watanabe, M., "Activity and Stability of Ordered and Disordered Co-Pt Alloys for Phosphoric Acid Fuel Cells" 141 : 2659-2668, 1994

16 Perry, M. L., "A Historical Perspective of Fuel Cell Technology in the 20th Century" 149 (149): 59-67, 2002