방전플라즈마소결법 적용 승온속도 변화에 따라 제조된 Fe-20Cu-1C 소결체 제조 및 특성평가 = Fabrication and Mechanical Property of Fe-20Cu-1C Compacts by SPS process with Different Heating Rate

다국어 초록 (Multilingual Abstract)

In this study, Fe-Cu-C alloy is sintered by spark plasma sintering (SPS). The sintering conditions are 60 MPa pressure with heating rates of 30, 60 and $9^{\circ}C/min$ to determine the influence of heating rate on the mechanical and microstructure properties of the sintered alloys. The microstructure and mechanical properties of the sintered Fe-Cu-C alloy is investigated by X-ray diffraction (XRD) and field-emission scanning electron microscopy (FE-SEM). The temperature of shrinkage displacement is changed at $450^{\circ}C$ with heating rates 30, 60, and $90^{\circ}C/min$. The temperature of the shrinkage displacement is finished at $650^{\circ}C$ when heating rate $30^{\circ}C/min$, at $700^{\circ}C$ when heating rate $60^{\circ}C/min$ and at $800^{\circ}C$ when heating rate $90^{\circ}C/min$. For the sintered alloy at heating rates of 30, 60, and $90^{\circ}C/min$, the apparent porosity is calculated to be 3.7%, 5.2%, and 7.7%, respectively. The hardness of the sintered alloys is investigated using Rockwell hardness measurements. The objective of this study is to investigate the densification behavior, porosity, and mechanical properties of the sintered Fe-Cu-C alloys depending on the heating rate.