촉매적 제탄(製炭)에 관한 시험 = Studies on the Catalytic charcoaling

다국어 초록 (Multilingual Abstract)

1. Objects
The experiments of catalytic aharonaling were carried out for the fallowing purposes.
(1) To determine the economically desirable amount of catalytic materials to be used when a catalytic charcoaling is practiced.
(2) To observe the rate of carbonization of non-treated charcoal wood when the catalytic charcoaling is proceeded in the same charcoal pit.
2. Meterials
(1) Small sample chips made of oak (Q. accutissima Carr.), measured by 0.5㎝ in width and thickness, respectively, and 1㎝ in length, were used as charcoal wood in each experiment.
(2) Ammonium chloride was used as a catalytic material and electric kiln as a charcoaling apparatus.
3. Experiment
(1) The sample chips were put into a electric oven for three hours at the temperature 60˚∼70℃ in order to reduce some water contents.
(2) Oven dried sample chips were then soaked for an hour in solution of ammonium chloride. Three kinds of solution were prepared, that is, 2.5%, 5%, and 10%, solution in which the amount of ammonium chloride used was weighed at the rate of 0.5%, 1.0%, and 2.0% to the total weight of the sample chips, resppectivelly.
(3) Soaked sample chips were put in the air for 12 hours to reduce some water contents, and then were put into electric oven for 2 hours at the temperature 105˚∼110℃.
(4) Dried sample chips were kept in a desiecator with control sample chips which were treated excarly the same process as the treated sample chips except only not using the ammonium chloride in the process of soking.
(5) Sample chips kept in the desiecator were used at random in each charcoaling experiment.
(6) Charcoaling in the electric kiln were carried out by using small crucibles with complete cover to reduce the amount of ash. At each charcoaling experiment four crucibles filled with sample ships, weighed about 20gr, were put into electuic kiln. The charcoaling was continued for an hour at the temperature 400˚∼450℃.
(7) In order to investigate the influence given by the gases produced during the catalytic charcoaling to the rate of carbonization of non-treated sample chips, the following experiment was done.
(a) A crueible was divided into two parts by inserting a fine iron net at the middle of the crucible, and then non-treated sample chips, weighed about 10gr, were put in the upper part of the crucible and treated sample chips, weighed also about 10gr, were put in the under part.
(b) The crucibles filled with two kinds of sample chips were put into a electric kiln for an hour at the temperature 400˚∼450℃.
4. Results.
Results for two replications (with four crucibles in one replication) for each experiment designed are as follows :
(1) The rats of carbonization of the non treated sample chips, and that of the treated sample chips with ammonium chloride at the rate of 1.5%, 1.0%, and 2.0% to the total weight of the sample chips used were averaged at 19.85%, 22.63%, 24.14%, and 26.60%, respectively.
(2) The rats of carbonization of the non-treated sample chips were averaged at (a) 20.04% (0.5% treatment), (b) 20.28% (1.0% treatment), and (c) 20.61% (2.0% treatment) when the treated sample chips were carbonized in the same crucible.