<P>In this study, we tried to fabricate the nanostructured bulk copper alloys by a severe plastic deformation process. The sheets of copper alloys (OFC, PMC90, and DLP) were heavily deformed to an equivalent strain of 6.4 by the accumulative rol...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107644385
2007
-
학술저널
3985-3989(5쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P>In this study, we tried to fabricate the nanostructured bulk copper alloys by a severe plastic deformation process. The sheets of copper alloys (OFC, PMC90, and DLP) were heavily deformed to an equivalent strain of 6.4 by the accumulative rol...
<P>In this study, we tried to fabricate the nanostructured bulk copper alloys by a severe plastic deformation process. The sheets of copper alloys (OFC, PMC90, and DLP) were heavily deformed to an equivalent strain of 6.4 by the accumulative roll-bonding (ARB) process. The microstructure and the mechanical property of the fabricated specimens were systematically investigated. The microstructure was finely subdivided with increasing the equivalent strain by the ARB process. The severely deformed copper alloys exhibited the ultrafine lamellar boundary structure where the mean lamella spacing was about 200 nm. The strength significantly increased with decreasing the lamella spacing in the ARB processed copper alloys. Especially, the tensile strength of the DLP alloys ARB processed by 8 cycles (the equivalent strain of 6.4) reached to 520 MPa, which was about three times higher than that of same materials with conventional grain size of 10-100 <I>μ</I>m. On the other hand, the total elongation greatly dropped only by 1 ARB cycle corresponding to an equivalent strain of 0.8, which was around 3%. However, the total elongation increased again with increasing the number of the ARB cycle, and it reached to 10% after 8 cycles. The recovery of the total elongation could be recognized in all studied copper alloys. The obtained stress-strain curves showed that the improvement of the total elongation was caused by the increase in the post-uniform elongation. It can be concluded that the nanostructured copper alloys sheets having high strength without a large loss of ductility could be fabricated by the ARB process.</P>
Hysteresis in a Carbon Nanotube Based Electroactive Polymer Microfiber Actuator: Numerical Modeling
Autothermal Reforming of Propane over Hydrotalcite-Like Catalysts Containing Promotor