The Si₃N₄/STS304 joints vacuum-brazed with four types of Cu-Ag-Ti brazing alloy was shearing-tested. For the joints showing interfacial fracture the position, morphology and microchemistry of reaction products on the fracture surface of Si₃N₄-...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A3233174
1993
Korean
436
KCI등재
학술저널
330-339(10쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
The Si₃N₄/STS304 joints vacuum-brazed with four types of Cu-Ag-Ti brazing alloy was shearing-tested. For the joints showing interfacial fracture the position, morphology and microchemistry of reaction products on the fracture surface of Si₃N₄-...
The Si₃N₄/STS304 joints vacuum-brazed with four types of Cu-Ag-Ti brazing alloy was shearing-tested. For the joints showing interfacial fracture the position, morphology and microchemistry of reaction products on the fracture surface of Si₃N₄- side was investigated by scanning electron microscope (SEM) equipped with energy-dispersive spectrometer (EDS). Types and fratures of interfacial reaction products observed on the fracture surface are following : first, titanium silicide that is a layer structure and contains the network-shaped microcrack ; second, iron titanium silicide that is a granular (grain size is about several hundred nanometer in dia.) and layer structure ; third, Fe-Ti compounds can be classified into Fe-Ti-Si-Cr and Fe-Ti-Cr systems, the former is the angular-type grains (of several micrometer in size) and the latter is a compound showing the brittle cleavage fracture ; fourth, Cu-Ti-Fe compound that is a granular (grain size is about several hundred nanometer in dia.) and layer structure. All the compound consisted of a granular structure showed a intergranular fracture. Interfacial fracture of Si₃N₄/STS 304 joints is classified into three types as following ; first, seperation (fracture) at the interface between Si₃N₄and titanium silicide ; second, complex fracture varying the path through each interface between reaction products ; third, a part of fracture occur in the second form, but a large part of fracture occur through the inner of reaction products. The shear strength of Si₃N₄/STS304 joints showing three types of interfacial fracture is below 42 ㎫, average 180 and 202 ㎫ respectively. Therefore, the more the strength of joints is high, the more fracture occur through the inner of reaction products than at the interface between reaction products.
목차 (Table of Contents)
급속응고한 Al-Fe-Mo-Si 계 합금분말 압출재의 고온 성질에 관한 연구
ZrO2/스테인리스강 접합체의 잔류응력분포에 관한 연구
8090 합금의 강도와 인성에 미치는δ' 과 S' 상의 크기와 분포의 영향
Fe73.5Si13.5B9Cu1Nb3 합금에서α-Fe 의 결정화 부피분율에 따른 자기적 특성과 미세조직의 변화