복합화력발전 내 배열회수 보일러용 소재(탄소강 계열 및 듀플렉스 스테인리스강(UNS S32205))의 황산농도에 따른 부식거동 비교 연구 = Comparative Study on the Corrosion Behavior of Materials in Heat Recovery Steam Generators for Combined Cycle Power Plant, Based on Sulfuric Acid Concentrations: Carbon Steels vs. Duplex Stainless Steel (UNS S32205)

다국어 초록 (Multilingual Abstract)

This study examined the effects of sulfuric acid concentrations on the corrosion behaviors of three types of commercial steels, conventional carbon steel (SA192), sulfuric acid dew resistant steel (S-TEN), and duplex stainless steel (S32205), considered to be potential materials for the heat recovery steam generator (HRSG) in combined cycle power plants. Based on the results of electrochemical polarization, immersion and wet-dry cycle tests, when exposed to a high sulfuric acid concentration (50%), SA192 and S-TEN exhibited higher corrosion resistance than S32205, which was due to the formation of a stable FeSO4 scale on the carbon steel materials. With prolonged exposure, S-TEN with slightly higher concentrations of Cu and Sb showed lower weight loss than SA192. Conversely, when subjected to low sulfuric acid concentrations (5 and 10%), S32205 exhibited passivation behavior, and showed significantly superior corrosion resistance (i.e., much smaller weight loss) than the other two steel samples. The examination of localized corrosion damages through cross-section observation using a scanning electron microscope revealed also that S32205 suffered less damages from the wet-dry cycling. The long-term superior corrosion resistance of duplex stainless steel in low sulfuric acid concentrations, compared to carbon steel and sulfuric acid due resistant steel, make it a promising candidate material for the HRSG in combined cycle power plants.

참고문헌 (Reference)

1 V. S. Moura, 59 : 1127-, 2008

2 S. S. A. Rehim, 50 : 2258-, 2008

3 C. Carcasci, 41 : 757-, 2000

4 W. M. M. Huijbregts, 51 : 173-, 2004

5 C. Zhongbing, 331 : 74-, 2013

6 C. Zheng, 241 : 327-, 2019

7 D. Fleig, 160 : 1142-, 2013

8 W. Zuo, 93 : 1666-, 2020

9 A. Usami, Nippon Steel 90-, 2004

10 T. Wang, Elsevier Science 497 : 2016

11 G. W. Whitman, 7 : 665-, 1924

12 A. Pardo, 48 : 1075-, 2006

13 Y. Z. Chen, 427 : L1-, 2007

14 J. H. Hong, 54 : 174-, 2012

15 H. E. Townsend, 57 : 497-, 2001

16 D. C. D. Santos, 165 : 46-, 2020

17 G. Yang, 15 : 6828-, 2021

18 L. Chen, 193 : 109903-, 2021

19 V. Muthupandi, 358 : 9-, 2003

20 Z. Panossian, 58 : 1-, 2012

21 M. J. Kim, 66 : 125005-, 2010

22 S. Dean, 24 : 21-, 1985

23 B. T. Ellison, 125 : 524-, 1978

24 L. Zhang, 54 : 5387-, 2009

25 박선아 ; 장승익 ; 김정구 ; 이병호 ; 윤정봉, "황산·염산 복합 내식강 개발: 2. 현장 적용성 평가를 통한 개발강의 신뢰성 검증" 대한금속·재료학회 52 (52): 857-872, 2014

26 박선아 ; 김정구 ; 이병호 ; 윤정봉, "황산·염산 복합 내식강 개발: 1. 저합금강의 내식성에 영향을 미치는 합금원소의 영향" 대한금속·재료학회 52 (52): 837-855, 2014

27 김예은 ; 박진성 ; 조동민 ; 홍승갑 ; 김성진, "슈퍼 오스테나이트계 스테인리스강의 시그마상 특성에 따른 부식거동 분석" 한국부식방식학회 19 (19): 203-210, 2020

28 S. Rajendrachari, "Voltammetry" Books on Demand 77-, 2019

29 R. A. Buchanan, "Handbook of Environmental Degradation of materials" William Andrew 81-103, 2005

30 김기태 ; 김영식, "Effects of Sulfuric Acid Concentration and Alloying Elements on the Corrosion Resistance of Cu-bearing low Alloy Steels" 한국부식방식학회 17 (17): 154-165, 2018

31 L. J. Malone, "Basic concepts of chemistry" Wiley 2000