졸-겔법으로 제작된 저온 TiO₂ 박막의 촉매농도에 따른 광분해 특성 분석 = Properties of Low-Temperature Sol-Gel TiO₂ Thin Films with Catalyst Content

다국어 초록 (Multilingual Abstract)

ILow-temperature $TiO_2$ sol was synthesized with various catalyst contents by using a sol-gel method. $TiO_2$ thin films were produced by a dip-coating method and their optical, structural and photocatalytic properties were examined. Transmittance of $TiO_2$ thin films with 0.10 mol, 0.25 mol, 0.50 mol and 0.75 mol catalyst content showed high transmittance in the visible range. XRD results showed the anatase-to-rutile phase transition was accelerated with increasing catalyst content and the crystallinity size of the $TiO_2$ thin films increased with increasing catalyst content. SEM results indicated that the particle size of the $TiO_2$ thin films was the smallest with catalyst content of 0.25 mol. Photocatalytic results showed that methylene blue was completely decomposed in the presence of anatase film prepared with 0.10 mol, 0.25 mol and 0.50 mol catalyst content.