레일표면손상이 접촉피로수명에 미치는 영향

다국어 초록 (Multilingual Abstract)

Rails are subjected to damage from rolling contact fatigue, which leads to defects such as cracks. Rolling contact fatigue damages on the surface of rail such as head check, squats are one of growing problems. Another form of rail surface damage, known as “Ballast imprint” has become apparent. This form of damage is associated with ballast particles becoming trapped between the wheel and the surface of rail. These defects are still one of the key reasons for rail maintenance and replacement. In this study, we have investigated whether the ballast imprint is an initiator of head check type cracks and effect of defect size using Finite element analysis. The FE analysis were used to investigate stresses and strains in subsurface of defects according to variation of defect size. Based on loading cycles obtained from FE analysis, fatigue analysis for each point was carried out.

참고문헌 (Reference)

1 전현규, "레일손상에 의한 윤중증가를 고려한 표면균열 성장예측" 한국정밀공학회 28 (28): 1078-1085, 2011

2 Dwyer-Joyce, R. S., "Wear and fatigue of railway track caused by contamination, sanding and surface damage" 2003

3 Zili, L., "Squat growth - Some observations and the validation of numerical predictions" 271 (271): 148-157, 2011

4 Cannon, D. F., "Rail rolling contact fatigue Research by the European Rail Research Institute" 191 (191): 1-13, 1996

5 "Rail defects"

6 Guo, J. B., "Modeling of rolling contact fatigue for hard machined components with process-induced residual stress" 26 (26): 605-613, 2004

7 Baumann, G., "Formation of white-etching layers on rail treads" 191 (191): 133-140, 1996

8 Han, C., "Evaluation of multiaxial fatigue criteria under irregular loading" 24 (24): 913-922, 2002

9 Kondo, K., "Cause, increase, diagnosis, countermeasures and elimination of Shinkansen shelling" 191 (191): 199-203, 1996

10 Jin, Y., "Analysis of white etching layer generated on rail surface" 19 (19): 17-22, 2005