Au/YBCO 박막의 크기가 퀜치 거동에 미치는 영향 = Size Effect on Quench Development in Au/YBCO Films

다국어 초록 (Multilingual Abstract)

We investigated the size effect on quench development in $Au/YBa_2Cu_3O_7$ (YBCO) thin film meander lines on sapphire substrates. The meander lines were fabricated by patterning YBCO films coated with gold layers. The lines were subjected to simulated AC fault current, and immersed in liquid nitrogen during the experiment. After the initial rapid rise, the resistance increased moderately and then slowly. In 4 inch-diameter meander lines, the period during which the resistance increased moderately was considerably longer than in 2 inch-diameter line. Moderate increase of resistance was originated from quench propagation. The film temperature was about 180 K at the point when the propagation was completed. The rate of resistance increase after the quench completion was not affected by the film size.

참고문헌 (Reference)

1 H. P. Kraemer, "Test of a 1 kA superconducting fault current limiter for DC applications" 15 : 1986-1989, 2005

2 Hye-Rim Kim, "Resistance of superconducting fault current limiters based on YBa2Cu3O7 thin films after quench completion" 372-376, 2002

3 Hye-Rim Kim, "Resistance Development in Superconducting Fault Current Limiters Prior to Quench Completion" 13 : 2032-2035, 2003

4 김혜림, "Resistance Development in Au/YBCO Thin Film Meander Lines under High-Power Fault Conditions" 한국초전도학회 8 (8): 81-86, 2006

5 K Yasuda, "Research & development of superconducting fault current limiter in Japan" 15 : 1978-1981, 2005

6 Hye-Rim Kim, "Initial quench development in uniform Au/Y-Ba-Cu-O thin films" 11 : 2414-2417, 2001

7 J. Bock, "CUL 10: Development and field-test of a 10 kV/10 MVA resistive current limiter based on bulk MCP-BSCCO 2212" 15 : 1955-1960, 2005

8 김혜림, "Au/YBCO 박막 곡선에서의 회복 분석" 한국초전도학회 9 (9): 119-125, 2007