Nanocrystalline Ni1−xZnxFe2O4 ( 0.0 ≤ x ≤ 0.8) ferrites have been synthesized by using an oxalic-acid-based precursor method. The X-ray diffraction (XRD) analysis revealed the formation of a single-phase spinel structure at very low annealing te...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A104319823
T. Anjaneyulu (Narasaraopet Engineering College) ; A. T. Raghavender (Nishitha College of Engineering and Technology) ; K. Vijaya Kumar (Jawaharlal Nehru Technological University Hyderabad) ; P. Narayana Murthy (Acharya Nagarjuna University) ; K. Narendra (V. R. Siddhartha Engineering College)
2013
English
KCI등재,SCI,SCIE,SCOPUS
학술저널
1114-1118(5쪽)
3
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
Nanocrystalline Ni1−xZnxFe2O4 ( 0.0 ≤ x ≤ 0.8) ferrites have been synthesized by using an oxalic-acid-based precursor method. The X-ray diffraction (XRD) analysis revealed the formation of a single-phase spinel structure at very low annealing te...
Nanocrystalline Ni1−xZnxFe2O4 ( 0.0 ≤ x ≤ 0.8) ferrites have been synthesized by using an oxalic-acid-based precursor method. The X-ray diffraction (XRD) analysis revealed the formation of a single-phase spinel structure at very low annealing temperature. The particle size was observed to decrease with increasing Zn content x. The lattice constants was observed to increase with increasing Zn content x due to large ionic radii of the zinc ion when compared to that of the nickel ion. Magnetic measurements at room temperature revealed that the magnetization did not change monotonically with increasing Zn content x. The coercivity and the remanence were observed to decrease with increasing non-magnetic Zn content x. The observed magnetic properties may be due to a reduction in the number of exchange interactions and the nanocrystalline size with increasing Zn content x.
참고문헌 (Reference)
1 X. He, 59 : 1941-, 2005
2 L. Yu, 288 : 54-, 2005
3 P. S. Anil Kumar, 27 : 293-, 1996
4 H. Su, 310 : 17-, 2007
5 J. L. Dormann, 2 : 1223-, 1990
6 N. Rezlescu, 6 : 5707-, 1994
7 A. E. Virden, 290-291 : 868-, 2005
8 A. M. El-Sayed, 28 : 363-, 2002
9 Z. Zhong, 155 : 193-, 2005
10 R. Valenzuela, 109 : 07A329-, 2011
1 X. He, 59 : 1941-, 2005
2 L. Yu, 288 : 54-, 2005
3 P. S. Anil Kumar, 27 : 293-, 1996
4 H. Su, 310 : 17-, 2007
5 J. L. Dormann, 2 : 1223-, 1990
6 N. Rezlescu, 6 : 5707-, 1994
7 A. E. Virden, 290-291 : 868-, 2005
8 A. M. El-Sayed, 28 : 363-, 2002
9 Z. Zhong, 155 : 193-, 2005
10 R. Valenzuela, 109 : 07A329-, 2011
11 S. E. Jacobo, 272-276 : 2253-, 2004
12 S. A. Saafar, 322 : 2369-, 2010
13 S. A. Morrison, 95 : 6392-, 2004
14 J. Sun, 28 : 855-, 2002
15 M. Younas, 44 : 345402-, 2011
16 S. Yan, 287 : 153-, 2006
17 E. Manova, 217 : 4-, 2010
18 C. Upadhyay, 260 : 188-, 2003
19 A. T. Raghavender, 509 : 7004-, 2011
20 A. R. Bueno, 105 : 229-, 2007
21 V. Sepelak, 234-236 : 617-, 1997
22 M. U. Rana, 52 : 389-, 2002
23 V. Sepelak, 257 : 377-, 2003
24 R. H. Kodama, 77 : 394-, 1996
25 R. H. Kodama, 59 : 6321-, 1999
26 Y. Matsuo, 37 : 2359-, 2001
27 E. C. Stoner, 240 : 599-, 1948
28 C. P. Bean, 30 : S120-, 1959
29 P. Yadoji, 98 : 269-, 2003
30 T. T. Srinivasan, 63 : 3789-, 1988
31 A. Goldman, "Modern Ferrite Technology" Springer 2006
32 B. D. Cullity, "Introduction to Magnetic Materials" John Wiley and Sons Publications 2009
33 J. Smit, "'Ferrites' Physical Properties of Ferrimagnetic Oxides in Relation to Their Technical Applications" Phillips 149-, 1959
Estimate of the Secondary Cancer Risk from Megavoltage CT in Tomotherapy
Feasibility of Bone Assessment by Using the Nonlinear Parameter in Trabecular Bone
학술지 이력
연월일 | 이력구분 | 이력상세 | 등재구분 |
---|---|---|---|
2023 | 평가예정 | 해외DB학술지평가 신청대상 (해외등재 학술지 평가) | |
2020-01-01 | 평가 | 등재학술지 유지 (해외등재 학술지 평가) | |
2011-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2009-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2007-01-01 | 평가 | SCI 등재 (등재유지) | |
2005-01-01 | 평가 | 등재학술지 유지 (등재유지) | |
2002-07-01 | 평가 | 등재학술지 선정 (등재후보2차) | |
2000-01-01 | 평가 | 등재후보학술지 선정 (신규평가) |
학술지 인용정보
기준연도 | WOS-KCI 통합IF(2년) | KCIF(2년) | KCIF(3년) |
---|---|---|---|
2016 | 0.47 | 0.15 | 0.31 |
KCIF(4년) | KCIF(5년) | 중심성지수(3년) | 즉시성지수 |
0.26 | 0.2 | 0.26 | 0.03 |