전기 제강로 분진(EAFD)으로부터 알칼리 금속 및 염화물 제거를 위한 수 세척 공정 운영인자 조사 = Investigation of Water-Washing Process Parameters for Removal of Alkali Metals and Chlorides from Electric Arc Furnace Dust (EAFD)

다국어 초록 (Multilingual Abstract)

The present study investigated the effect of a water-washing process, which is part of the acid hydrometallurgical process for recovery of high purity of zinc, on the removal of alkali metals and chlorides (Na, K, Ca, Cl) from Electric arc furnace dust (EAFD). Two EAFD samples with different properties were characterized by particle size, XRD and element analysis, and their washing efficiencies (%) on alkali metals and chlorides were compared according to pH, washing time, liquid to solid (L/S) ratio and number of washings. The results show that the alkali metals and chlorides could be effectively removed by the washing (at L/S ration of 3 for more than 30 min., pH 10~11) while minimizing loss of zinc (<0.1%), in which the washing efficiency was Na-78%, K-76%, Cl >99%, respectively. Na and K could be removed up to 97% and 89% respectively by 3 times of repeated washings. With increased sample volume (10 times) of the mixed (1:1, w/w) sample with two types of EAFD, it was confirmed that the pH(10~11) can be used as the main process control parameter for the washing of the alkali metals regardless of EAFD properties.

국문 초록 (Abstract)

본 연구에서는 전기 제강로 분진(EAFD)으로부터 고 순도의 아연회수를 위한 산 습식법 중 알칼리 금속 및 염화물(Na, K, Cl) 제거를 위한 적정 수 세척공정의 운영조건에 대해 조사하였다. 서로 다른 성상을 가지는 두 종류의 EAFD 시료를 대상으로 원소분석, XRD, 입도 분석 등의 물리화학적 특성을 분석하였고, 세척액의 pH, 세척시간, 고액비(mL/g) 및 세척반복횟수 등에 따른 알칼리 금속 및 염화물의 세척효율(%)을 비교하였다. 연구 결과, EAFD 내 알칼리 금속과 염화물은 고액비 3, 세척시간>30, pH 10~11의 조건에서 아연과 철의 손실을 최소화하면서(<~0.1%) 효과적으로 제거할 수 있었으며, 1회 세척시 Na-78%, K-76%, Cl >99%의 세척효율을 보였다. Na와 K는 3회 반복 세척 시 각각 97%, 89%까지 제거 가능하였다. 두종류의 EAFD 혼합(1:1)시료를 대상으로 시료 용량을 늘려(10배) 수행한 실험 결과에서도 세척액의 최종 pH 10~11에서 Zn의손실 없이 Na, K, Cl 등을 효과적으로 제거 가능함을 확인하였다.

참고문헌 (Reference)

1 Langová, Š., "Zinc recovery from steelmaking wastes by acid pressure leaching and hematite precipitation" 101 : 171-173, 2010

2 Lutandula, M. S., "Zinc oxide production through reprocessing of the electric arc furnace flue dusts" 1 : 600-603, 2013

3 Bruckard, W. J., "Water leaching and magnetic separation for decreasing the chloride level and upgrading the zinc content of EAF steelmaking baghouse dusts" 75 : 1-20, 2005

4 Langová, Š., "Selective leaching of zinc from zonc ferrite with hydrochloric acid" 95 : 179-182, 2009

5 Behnagady, B., "Selective leaching of zinc from hazardous As-bearing zinc plant purification filter cake" 117 : 564-574, 2017

6 Jha, M. K., "Review of hydrometallurgical recovery of zinc from industrial wastes" 33 : 1-22, 2001

7 Chen, W. S., "Removal of chloride from electric arc furnace dust" 190 : 639-644, 2011

8 Fernández-Olmo, I., "Modeling of zinc solubility in stabilized/solidified electric arc furnace dust" 144 : 720-724, 2007

9 Martins, F. M., "Mineral phases of weathered and recent electric arc furnace dust" 154 : 417-425, 2008

10 Montenegro, V., "Hydrometallurgical treatment of steelmaking Electric Arc Furnace Dusts (EAFD)" 44B : 1058-1069, 2013

11 Oustadakis, P., "Hydrometallurgical process for zinc recovery from electric arc furnace dust (EAFD): Part I: Characterization and leaching by diluted sulfuric acid" 179 : 1-7, 2010

12 Tsakiridis, P. E., "Hydrometallurgical process for zinc recovery from electric arc furnace dust (EAFD). Part II: Downstream processing and zinc recovery by electrowinning" 179 : 8-14, 2010

13 Leclerc, N., "Hydrometallurgical extraction of zinc from zinc ferrites" 70 : 175-183, 2003

14 Shawabkeh, R. A., "Hydrometallurgical extraction of zinc from Jordanian electric arc furnace dust" 104 : 61-65, 2010

15 Montenegro, V., "Hydrometallurgical Treatment of EAF Dust by Direct Sulphuric Acid Leaching at Atmospheric Pressure" 7 (7): 1531-1548, 2016

16 Sekula, R., "Electric arc furnace dust treatment: investigation on mechanical and magnetic separation methods" 19 : 271-275, 2001

17 Wang, Q., "Effects of waterwashing pretreatment on bioleaching of heavy metals from municipal solid waste incinerator fly ash" 162 : 812-818, 2009

18 Guézennec, A. G., "Dust formation by bubble-burst phenomenon at the surface of a liquid steel bath" 44 (44): 1328-1333, 2004

19 Zhu, F., "Chlorides behavior in raw fly ash washing experiments" 178 : 547-552, 2010

20 Machado, J. G. M. S., "Chemical, physical, structural and morphological characterization of the electric arc furnace dust" 136 : 953-960, 2006

21 Sofiliæ, T., "Characterization of steel mill electric arc furnace dust" 109 : 59-70, 2004

22 Laforest, G., "Characterization and leachability of electric arc furnace dust made from remelting of stainless steel" 135 : 156-164, 2006

23 Kukurugya, F., "Behavior of zinc, iron and calcium from electric arc furnace (EAF) dust in hydrometallurgical processing in sulfuric acid solutions: Thermodynamic and kinetic aspects" 154 : 20-32, 2015

24 Havlik, T., "Atmospheric leaching of EAF dust with diluted sulphuric acid" 77 : 41-50, 2005