Physical properties of various Sealants with tooth components|RISS 상세보기

다국어 초록 (Multilingual Abstract)

Objectives: In order to develop the new sealant material with bio-material, under 40 of micro-granules and 0.07g of the enamel and dentin powers added to commercia sealant and flow able Resin material. The compressive strength, adaptability and bio-compatability were measured and surface appearances were observed with SEM findings

Methods: 57 of (Small sized) cylinder type specimens as 3 of diameter and 2 of height were produced to measure the compressive strength and adaptability test, and 57 samples were applied for SEM findings, through classified as sealant with enamel, or dentin or cementum, flowable resin with the same bio-components.

Results: The height in compressive strength was proved in commercial sealant group otherwise the adaptability was revealed as the highest in sealant with dentin powder group. Some cracks or poruses were found SEM findings in sealant group but it was decreasing tendency of them in sealant with dentin powder group.

Conclusion: Sealant with dentin group is the best for Bio-compatability and recommended it to be developed as a new Bio-material for sealant.

번역하기

목차 (Table of Contents)

1. Introduction 2
2. Materials & Method 3
2.1. Materials 3
2.2. Methods 3
2.2.1. Measuring of compressive strength 3

1. Introduction 2
2. Materials & Method 3
2.1. Materials 3
2.2. Methods 3
2.2.1. Measuring of compressive strength 3
2.2.2. Measuring of adaptability 4
2.2.3. Examining of specimen surface 4
2.2.4. Bio-compatability test 4
3. Research Result 5
3.1. Compressive strength measurement 5
3.2. Adaptability measurement 6
3.3. SEM images for surface examine 7
3.4. SEM images for Bio-compatability according to the duration in Taliva solution 9
4. Discussion 9
5. Conclusion 11

참고문헌 (Reference)

1 Duangthip D, "Variables contributing to the quality of fissure sealants used by general dental practitioners" 28 (28): 756-764, 2003

2 Kwang-Sik Park, "The strength and hardness of the sealant containing the filler component" 대한예방치과학회 3 (3): 69-80, 2007

3 Grewal N, "The effect of fissure morphology and eruption time on penetration and adaptation of pit and fissure sealants: An SEM study" 26 (26): 59-63, 2008

4 Antonson SA, "Surface protection for newly erupting firstmolars" 27 (27): 46-52, 2006

5 Joseph VP, "Some "sealants" seal--a scanning electron microscopy(SEM) investigation" 105 (105): 362-368, 1994

6 Cuto EI, "Sealing of pit and fissure with an adhesive resin:its use in caries prevention" 75 : 121-128, 1967

7 Kane B, "Sealant adaptation and penetration into occlusal fissures" 22 (22): 89-91, 2009

8 Ho-Young Jung, "SEM finding on the pit & fissure sealants method and sealants material" 대한예방치과학회 4 (4): 156-167, 2008

9 Gomez S, "SEM analysis of sealant penetration inposterior approximal enamel carious lesions in vivo" 10 (10): 151-156, 2008

10 Harris NO, "Primary preventive dentistry. 6th ed" Prentice Hall 285-318, 2004