텅스텐 할로겐 램프를 사용하는 ZMR공정의 매개변수 최적화에 관한 연구 = A Study on Optimization of Process Parameters in Zone Melting Recrystallization Using Tungsten Halogen Lamp

다국어 초록 (Multilingual Abstract)

Some solutions to several major problems in ZMR such as agglomeration of polysilicon, slips and local substrate melting are described. Experiments are performed with varying polysilicon thickness and capping oxide thickness. The aggmeration can be eliminated when nitrogen is introduced at the capping oxide layer-to-polysilicon interface and polysilicon-to-buried oxide layer interface by annealing the SOI samples at $1100^{\circ}$ in $NH_3$ ambient for three hours. The slips and local substrate melting are removed when the back surface of silicon substrate is sandblasted to produce the back surface roughness of about $20{\mu}m$. The subboundary spacing increases with increasing polysilicon thickness and the uniformity of recrystallized SOI film thickness improves with increasing capping oxide thickness, improving the quality of recrystallized SOI film. When the polysilicon thickness is about $1.0{\mu}m$ and the capping oxide thickness is $2.5{\mu}m$, the thickness variation of the recrystallized SOI film is about ${\pm}200{\AA}$ and the subboundary spacing is about $70-120{\mu}m$.