BaO-GeO2-La2O3-ZnO 계에 있어서 BaO 첨가량 변화에 따른 광학 특성 = Optical Properties according to BaO Addition for BaO-GeO2-La2O3-ZnO System

다국어 초록 (Multilingual Abstract)

In this study, Barium Germanium glasses were prepared with a composition of xBaO-(72-x)GeO2-8La2O3-20ZnO where x = 16.0, 18.0, 20.0, 22.0 and 24.0 mol% respectively. Their physical and optical properties, such as refractiveness index, glass transition temperature (Tg), softening temperature (Ts), transmittance and Knoop hardness were studied. The results showed that refractive index, Tg, Ts and coefficient of thermal expansion (CTE) increased with increasing BaO concentration. The refractive index of all the prepared samples was observed between 1.7811 to 1.7881. The Abbe number was calculated by formula using nd (589.3 nm), nf (656.3 nm) and nc (486.1 nm) and observed to be between 38 to 40. The Abbe number of the prepared sample was similar to that of BaO and GeO2. The transmittance of the prepared glasses was observed to be between 80 ~ 82 % throughout the range from 200 nm to 800 nm. Knoop hardness divided into seven steps were measured 5 class (≥ 450 ~ < 550) of all prepared samples.

참고문헌 (Reference)

1 P. Hartmann, 49 : D157-, 2010

2 R. D. Shannon, 31 : 931-, 2002

3 V. Greco, 32 : 6219-, 1993

4 E. S. Lim, 27 : 825-, 2007

5 J. T. Littleton, 4 : 224-, 1920

6 A. V. Anan’ev, 354 : 3049-, 2008

7 S. Sebastiani, 13 : 1696-, 2005

8 S. Valligatla, 73 : 012006-, 2015

9 M. Micoulaut, 18 : R753-, 2006

10 D. L. Wood, 21 : 4276-, 1982

11 Poulain, 56 : 1-, 1981

12 S. Kohara, 303 : 1649-, 2004

13 Z. Mao, 41 : S51-, 2015

14 H. Bach, "The Properties of Optical Glass" Springer 169-, 1998

15 Schott, "The Catalog Optical Glass" Schott Optical Glass Inc 1987

16 "SCHOTT, TIE-35: Transmittance of optical glass, 2020from SCHOTT Technical Information database"

17 M. N. Polyanskiy, "Refractive Index INFO On the Web"

18 E. Hecht, "Optics" Pearson Education 1-, 2006

19 A. Zakery, "Optical Nonlinearities in Chalcogenide Glasses and their Applications" Springer Series in Optical Science 726-, 2007

20 "HOYA GROUP Optics Division, Mechanical Properties On the Web"