계면 흡착에 의한 InAs/GaSb 초격자의 응력변조 효과 = Effects of Interface Soaking on Strain Modulation in InAs/GaSb Strained-Layer Superlattices

다국어 초록 (Multilingual Abstract)

In this study, the interface soaking effect in InAs/GaAs strained-layer superlattice (SLS) on crystalline phase modulation has been analyzed by the x-ray diffraction (XRD) curve. The strain variation induced by As and/or Sb soaking was determined by the separation angle between the substrate peak and the 0th-order superlattice satellite peak in the XRD spectra. Contrated that the As/InAs soaking arises minor GaAs-like interfacial layer, the Sb/GaSb soaking induces InSb-like one. The Fourier-transformed curves of the Pendellosung interference oscillation shows that the optimum soaking times of As/InAs and Sb/GaSb are 2 sec and 12 sec, at which the highest crystallineity has, respectively. An anomalous twin-peak phenomenon that a satellite peak splits into two peaks was observed in the SLS structure co-soaked by As and Sb at InAs${\rightarrow}$GaSb interfaces. We suggest that it may be resulted from coexistence of two kinds crystalline phases of InAsSb and GaAsSb due to intermixing of In${\leftrightarrow}$Ga and Sb${\leftrightarrow}$As.

국문 초록 (Abstract)

본 연구에서는 InAs/GaSb 응력초격자(SLS)의 계면 흡착(soaking)에 의한 응력변조 효과를 X선회절(XRD)을 통하여 분석하였다. As과 Sb 흡착에 의하여 유도된 응력의 변화는 XRD 곡선의 기판피크과 0차 위성피크 사이의 분리각으로부터 조사하였으며, As/InAs 흡착은 약간의 GaAs-like 계면층을 유발하는 반면, Sb/GaSb 흡착은 InSb-like 계면상을 유도하는 것으로 분석되었다. Pendellosung 간섭진동의 Fourier 변환 곡선을 이용하여, [InAs/GaSb]-SLS 성장에서 결정성이 가장 우수한 최적 As/InAs와 Sb/GaSb의 흡착시간은 각각 2 sec와 10 sec임을 밝혔다. InAs${\rightarrow}$GaSb 계면에 As과 Sb를 동시에 흡착시킨 SLS에서 XRD 위성피크가 2개로 분할되는 특이한 쌍정현상이 관측되었는데, 이것은 계면에서 In${\leftrightarrow}$Ga 및 Sb${\leftrightarrow}$As 상호혼합에 의한 InSbAs와 GaAsSb의 2종의 결정상이 공존함으로써 발생한 현상으로 추정된다.

참고문헌 (Reference)

1 D. L. Smith, 62 : 2545-, 1987

2 J. H. Li, 95 : 096104-, 2005

3 P. Piquini, 77 : 115314-, 2008

4 E. Plis, 91 : 133512-, 2007

5 S. J. Lee, 95 : 102106-, 2009

6 S. Mou, 92 : 153505-, 2008

7 S. Maison, 89 : 151109-, 2006

8 A. Khoshakhlagh, 91 : 263504-, 2007

9 E. Crobin, 16 : 263-, 2001

10 H. S. Kim, 92 : 183502-, 2008

11 S. J. Lee, 2010

12 S. Maison, 89 : 151109-, 2006

13 B. -M. Nguyen, 91 : 163511-, 2007

14 B. J. Spencer, 64 : 235318-, 2001

15 X. B. Zhang, 287 : 545-, 2006

16 G. C. Dente, 86 : 1420-, 1999

17 X. B. Zhang, 90 : 131110-, 2007

18 A. Fasolino, 33 : 8889-, 1986

19 J. Steinshnider, 85 : 2953-, 2000

20 H. Kroemer, 20 : 196-, 2004

21 김준오, "고분해능 XRD 분석에 의한 InAs/GaSb 응력초격자 구조의 성장 최적화 연구" 한국진공학회 18 (18): 245-253, 2009

22 S. J. Lee, "On the Temperature Dependence of the Mid-Infrared Cuto Energy in an InAs/GaSb Type-II Superlattice Photodetector" 한국물리학회 54 (54): 280-283, 2009