후열처리에 따른 스퍼터된 ZnO:Al 박막의 전기적, 광학적 특성 = Optical and Electrical Properties of Sputtered ZnO:Al Thin Films with Various Annealing Temperature

다국어 초록 (Multilingual Abstract)

ZnO:Al thin films deposited by RF magnetron sputtering were post-annealed and the electrical and optical properties of ZnO:Al thin films were investigated before and after anneling. We confirmed that the ZnO:Al thin film was affected by post-annealing temperature. As post-annealing temperature increases, crystallinity and transmittance in visible area (400~800 nm) of ZnO:Al thin films decreased. While sheet resistance of thin films increased sharply with increasing to $400^{\circ}C$. This result is due to reduce of carrier concentration caused by absorption of $O_2$ or $N_2$ at surface of thin film.

국문 초록 (Abstract)

RF magnetron sputtering 법을 이용하여 증착된 ZnO:Al 박막을 열처리하여 열처리 전 후 ZnO:Al 박막의 전기적, 광학적 특성을 연구하였다. 열처리 온도에 따라 ZnO:Al 박막의 특성이 많이 영향 받음을 확인하였다. 열처리 온도가 증가함에 따라 ZnO:Al 박막의 결정성과 가시광선 영역(400~800 nm)에서 투과도는 감소함을 보였다. 반면, 박막의 비저항은 $400^{\circ}C$로 열처리 온도가 증가함에 따라 급격히 증가하였다. 이는 박막 표면에 $O_2$ 또는 $N_2$가 흡착하여 캐리어 농도 감소에 의한 것으로 판단된다.

참고문헌 (Reference)

1 S. W. Cho, 98 : 023102-, 2011

2 S. S. Lin, 185 : 254-, 2004

3 C. H. Kuo, 11 : H269-, 2008

4 S. J. Yun, 47 : 3067-, 2008

5 Y. M. Lu, 72 : 269-, 2001

6 M. Lorenz, 47 : 2205-, 2003

7 A. Maldonado, 90 : 742-, 2006

8 K. Ellmer, 34 : 3097-, 2001

9 S. Major, 33 : R17-, 2000

10 B. P. Shantheyanda, 29 : 051514-, 2011

11 M. Y. Zhang, 98 : 051904-, 2011

12 W. H. Kim, 158 : D495-, 2011

13 S. H. Jeong, 447 : 105-, 2004

14 H. Tong, 257 : 4906-, 2011

15 T. Minami, 520 : 3803-, 2012

16 정성진, "RF 마그네트론 스퍼터링법으로 제작된 Ga-doped ZnO 박막의 공정압력에 따른 전기적, 광학적 특성" 한국진공학회 21 (21): 17-21, 2012

17 김덕규, "RF Magnetron Sputtering법으로 제작한 ZnO:Al 박막의 초기 압력에 따른 특성" 한국진공학회 20 (20): 141-145, 2011

18 B. D. Cullity, "Elements of X-ray Diffraction" Addison-Wesley 102-, 1978