청색발광소자를 위한 I $n_{x}$G $a_{1-x}$N 결정성장 및 특성평가 = Growth and Characterization of I $n_{x}$G $a_{1-x}$N Epitaxial Layer for Blue Light Emitter

다국어 초록 (Multilingual Abstract)

Single crystalline I $n_{x}$G $a_{1-x}$ N thin film was grwon by MOCVD on (001) sapphire substrate for the blue light emitting devices. A good quality of I $n_{0.13}$G $a_{0.87}$N/GaN heterostructure grwon above 700.deg. C was confiremed by various characterization techniques of AFM, RHEED and DC-XRD. Through PL measurement at room temperautre for the Si-Zn co-doped I $n_{x}$G $a_{a-x}$N/GaN structure grwon at 800.deg. C to obtain blue wavelength emission, 460-470 nm and 425 nm emission peak were observed, which are believed to be from donor-to-acceptor pair transition and band edge emission of In/x/G $a_{1-x}$ N, respectively. The result of PL measurement of the undoped MQW I $n_{x}$G $a_{1-x}$ N layer at low temperature confirmed that the strong MQW peak was resulted by exciton from the GAN barrier and carrier of DA pair confined into the well layer.ll layer.yer.r.