<P><B>Abstract</B></P> <P>A chemical reduction process was proposed to recover copper from the retentate of polyelectrolyte enhanced ultrafiltration (PEUF). Three polyelectrolytes (PSS, PAA, and PEI) containing various f...
http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
https://www.riss.kr/link?id=A107454504
2018
-
SCIE,SCOPUS
학술저널
113-120(8쪽)
0
상세조회0
다운로드다국어 초록 (Multilingual Abstract)
<P><B>Abstract</B></P> <P>A chemical reduction process was proposed to recover copper from the retentate of polyelectrolyte enhanced ultrafiltration (PEUF). Three polyelectrolytes (PSS, PAA, and PEI) containing various f...
<P><B>Abstract</B></P> <P>A chemical reduction process was proposed to recover copper from the retentate of polyelectrolyte enhanced ultrafiltration (PEUF). Three polyelectrolytes (PSS, PAA, and PEI) containing various functional groups and molecular weights were studied to explore their effects on the copper removal in PEUF and on the copper recovery by chemical reduction under various pH conditions. With PSS which contains sulfonic group, copper was removed reasonably well (ca. 75%) by PEUF even under acidic pH value of 3. With PAA which contains carboxylic group, copper removal was a bit low (∼60%) under pH 3.0 but increased substantially at pH 4.0. A branched PEI having amine group achieved the highest Cu removal of 94% at pH 3. The copper removal efficiency decreased slightly with increasing pH due to the high permeation of PEI through membrane.</P> <P>Chemical reduction achieved the complete copper recovery for solution containing PSS. The copper recovery efficiencies were more than 95% for PAA solution with pH values ranging from 3 to 9 at reaction time of one hour. For PEI, the recovery efficiencies ranged from 20 to 96% and were pH dependent. Aggregated and settled readily copper particles were produced by chemical reduction in PSS solution. XRD analysis identified cuprous oxide in all of the samples. Dependent of pH and polyelectrolytes, additional peaks matching those of elemental copper were identified. TGA analysis showed that solids produced from PSS and PAA systems contained no polyelectrolytes while solid collected from PEI system contained 32% of polyelectrolyte.</P> <P><B>Highlights</B></P> <P> <UL> <LI> Polyelectrolytes with different functional groups and MW were applied in PEUF. </LI> <LI> Effects of polyelectrolytes and pH on the reduction of copper were studied. </LI> <LI> Both Cu<SUB>2</SUB>O and Cu<SUP>0</SUP> were identified by XRD analysis of solids obtained. </LI> </UL> </P>