폴리에스테르 織物의 Benzyl alcohol과 Sodium hydroxide 混合水溶液에 依한 減量加工에 關한 硏究 = (A) Study on the Weight Reducing of Polyester Fabric by Aqueous Solution of Benzyl Alcohol and Sodium Hydroxide Mixture

다국어 초록 (Multilingual Abstract)

polyester georgette fabric was floated in various conditions of sodium hydroxide solution and sodium hydroxide/benzyl alcohol mixture solution. The effects of benzyalcohol addition in sodium hydroxide solution were measured as the weight loss, improvement of handle and changes of breaking strength and elongation of fabric.
The results were expressed as follows ;
The tendency of weight loss in the NaOH solution was accelerated by the addition of small amount of benzyl alcohol (1-2%).
By the addition of small amount of benzylalcohol, it was possible to lower the treating temperature and to reduce the NaOH concentration in alkali treatment of polyester fabric.
The fabric treated in NaOH/benayl alcohol mixture solution showed lower weight loss and higher breaking strength and elongation than that in NaOH solution, when the same handle improvement was concerned.

목차 (Table of Contents)

• 목차 = ⅰ
• Ⅰ. 序論 = 1
• Ⅱ. 實驗 = 3
• 1. 試料 및 試藥 = 3
• 2. 實驗方法 = 3
• 1) 수산화나트륨용액 處理 = 3
• 2) 수산화나트륨과 benzyl alcohol 混合水溶液에 의한 處理 = 3
• 3) Handle의 測定 = 4
• 4) 引張强力 및 伸度의 測定 = 5
• Ⅲ. 實驗結果 및 考察 = 6
• 1. 수산화나트륨 처리에 의한 重量減少와 物性變化 = 6
• 2. NaOH/benzyl alcoho l混合水溶液處埋에 의한 重量減少와 特性變化 = 7
• 3. 수산화나트륨 단독처리와 NaOH/benzyl alcohol 混合處理의 結果比較 = 19
• Ⅳ. 結論 = 23
• 參考文獻 = 24
• ABSTRACT = 25