RISS 검색 - 국내학술지논문 상세보기

다국어 입력

あぁかがさざただなはばぱまやゃらわゎんいぃきぎしじちぢにひびぴみりうぅくぐすずつづっぬふぶぷむゆゅるえぇけげせぜてでねへべぺめれおぉこごそぞとどのほぼぽもよょろを

アァカサザタダナハバパマヤャラワヮンイィキギシジチヂニヒビピミリウゥクグスズツヅッヌフブプムユュルエェケゲセゼテデヘベペメレオォコゴソゾトドノホボポモヨョロヲ ―

http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.

변환된 중국어를 복사하여 사용하시면 됩니다.

예시)

中文 을 입력하시려면 zhongwen을 입력하시고 space를누르시면됩니다.
北京 을 입력하시려면 beijing을 입력하시고 space를 누르시면 됩니다.

ㅥ ㅦ ㅧ ㅨ ㅩ ㅪ ㅫ ㅬ ㅭ ㅮ ㅯ ㅰ ㅱ ㅲ ㅳ ㅴ ㅵ ㅶ ㅷ ㅸ ㅹ ㅺ ㅻ ㅼ ㅽ ㅾ ㅿ ㆀ ㆁ ㆂ ㆃ ㆄ ㆅ ㆆ ㆇ ㆈ ㆉ ㆊ ㆋ ㆌ ㆍ ㆎ

Α Β Γ Δ Ε Ζ Η Θ Ι Κ Λ Μ Ν Ξ Ο Π Ρ Σ Τ Υ Φ Χ Ψ Ω α β γ δ ε ζ η θ ι κ λ μ ν ξ ο π ρ σ τ υ φ χ ψ ω

á à Á À é è É È ç Ç ê

Ä Ö Ü ä ö ü ß

ְ ֳ ֲ ֱ ָ ַ ֵ ֶ ִ ֹ ּ ֻ ׂ ׁ ּ פ ם ן ו ט א ר ק ף ך ל ח י ע כ ג ד ש ץ ת צ מ נ ה ב

‘ ’ “ ” 〔〕〈〉「」『』【】＂（）［］｛｝

± × ÷ ≠ ≤ ≥ ∞ ∴ ♂ ♀ ∠ ⊥ ⌒ ∂ ∇ ≡ ≒ ≪ ≫ √ ∽ ∝ ∵ ∫ ∬ ∈ ∋ ⊆ ⊇ ⊂ ⊃ ∪ ∩ ∧ ∨ ￢ ⇒ ⇔ ∀ ∃ ∮ ∑ ∏ ＋－＜＝＞

、。 · ‥ … ¨ 〃 ― ∥ ＼ ∼ ´ ～ ˇ ˘ ˝ ˚ ˙ ¸ ˛ ¡ ¿ ː ！＇，．／：；？＾＿｀｜

½ ⅓ ⅔ ¼ ¾ ⅛ ⅜ ⅝ ⅞ ¹ ² ³ ⁴ ⁿ ₁ ₂ ₃ ₄

Æ Ð Ħ Ĳ Ł Ø Œ Þ Ŧ Ŋ æ đ ð ħ ı ĳ ĸ ŀ ł ø œ ß þ ŧ ŋ ŉ

А Б В Г Д Е Ё Ж З И Й К Л М Н О П Р С Т У Ф Х Ц Ч Ш Щ Ъ Ы Ь Э Ю Я а б в г д е ё ж з и й к л м н о п р с т у ф х ц ч ш щ ъ ы ь э ю я

′ ″ ℃ Å ￠￡￥ ¤ ℉ ‰ ＄％Ｆ￦㎕㎖㎗ ℓ ㎘㏄㎣㎤㎥㎦㎙㎚㎛㎜㎝㎞㎟㎠㎡㎢㏊㎍㎎㎏㏏㎈㎉㏈㎧㎨㎰㎱㎲㎳㎴㎵㎶㎷㎸㎹㎀㎁㎂㎃㎄㎺㎻㎽㎾㎿㎐㎑㎒㎓㎔ Ω ㏀㏁㎊㎋㎌㏖㏅㎭㎮㎯㏛㎩㎪㎫㎬㏝㏐㏓㏃㏉㏜㏆

§ ※ ☆ ★ ○ ● ◎ ◇ ◆ □ ■ △ ▽ → ← ↑ ↓ ↔ 〓 ◁ ◀ ▷ ▶ ♤ ♠ ♡ ♥ ♧ ♣ ⊙ ◈ ▣ ◐ ◑ ▒ ▤ ▥ ▨ ▧ ▦ ▩ ♨ ☏ ☎ ☜ ☞ ¶ † ‡ ↕ ↗ ↙ ↖ ↘ ♭ ♩ ♪ ♬ ㉿㈜ № ㏇ ™ ㏂㏘ ℡ ＃＆＊＠ ª º

ⅰ ⅱ ⅲ ⅳ ⅴ ⅵ ⅶ ⅷ ⅸ ⅹ Ⅰ Ⅱ Ⅲ Ⅳ Ⅴ Ⅵ Ⅶ Ⅷ Ⅸ Ⅹ

ا ب ت ث ج ح خ د ذ ر ز س ش ص ض ط ظ ع غ ف ق ک ل م ن ه و ی

닫기

최근 검색 목록
전체삭제 닫기

RISS 인기검색어

Floating zone 법에 의한 $SrTiO_3$단결정 성장 = $SrTiO_3$ single crystal growth by floating zone method

한글로보기

https://www.riss.kr/link?id=A101123045

저자

전병식 ; 조현 ; 오근호 ; Jeon, Byong-Sik ; Cho, Hyun ; Orr, Keun-Ho
발행기관
한국결정성장학회
학술지명
한국결정성장학회지(Journal of the Korean Crystal Growth and Crystal Technology )
권호사항

Vol.5 No.2 [1995]
발행연도
1995
작성언어
Korean
등재정보
KCI등재,ESCI
자료형태
학술저널
발행기관 URL
http://www.kacg.net
수록면

87-93(7쪽)
제공처
ScienceON
소장기관

0
상세조회
0
다운로드
0
내보내기

서지정보 열기

부가정보

다국어 초록 (Multilingual Abstract)

Strontium titanate single crystal was grown by floating wne method. Growth conditions are as follows; at air atmosphere, rotation rate of upper and lower shafts were 20 - 25 rpm, 15 - 20 rpm respectively and growth rate was 3 mmlhr. As grown crystal was light brown color and transparent. After annealing, color was faded away. Growth direction was [112] direction and it was confirmed that grown crystal has $SrTiO_3$single phase and stoichiometric composition by XRD and EDS.
Etch pit pattern was investigated after chemical etching in $350^{\circ}C$, KOH solution for 5 min and dielectric constant was measured at the range of room temperature ~ $350^{\circ}C$ .

번역하기

Strontium titanate single crystal was grown by floating wne method. Growth conditions are as follows; at air atmosphere, rotation rate of upper and lower shafts were 20 - 25 rpm, 15 - 20 rpm respectively and growth rate was 3 mmlhr. As grown crystal w...

Strontium titanate single crystal was grown by floating wne method. Growth conditions are as follows; at air atmosphere, rotation rate of upper and lower shafts were 20 - 25 rpm, 15 - 20 rpm respectively and growth rate was 3 mmlhr. As grown crystal was light brown color and transparent. After annealing, color was faded away. Growth direction was [112] direction and it was confirmed that grown crystal has $SrTiO_3$single phase and stoichiometric composition by XRD and EDS.
Etch pit pattern was investigated after chemical etching in $350^{\circ}C$, KOH solution for 5 min and dielectric constant was measured at the range of room temperature ~ $350^{\circ}C$ .