Polyetherimide 접착제의 표면 처리에 따른 MCM-D 계면 접착력 및 고온고습 신뢰성 변화에 관한 연구 = A Study on the Effect of Polyetherimide Surface Treatment on the Adhesion and High Temperature/High Humidity Reliability of MCM-D Interface

다국어 초록 (Multilingual Abstract)

The adhesion strength and high temperature/high humidity reliability of polyetherimide (PEI) adhesive on silicon wafer after being treated by each reactive ion etching (RIE) Aluminum (Al)-chelate adhesion promoter were investigated. 180$^{\circ}$ peel test and <85$^{\circ}C$ 85%> humidity test were performed for the initial adhesion strength and high temperature/high humidity reliability, respectively. For investigating surface effect scanning electron microscope (SEM), atomic force microscope (AFM), deionized (DI)-water contact angle studies were carried out. To investigate RIE effect, PEI was treated with $^O_2$ RIE, and then laminated. The initial peel strength increased slightly from 1.6 kg/cm for the first 2 minutes, and then decreased. High temp/high humid resistance decreased rapidly by RIE etching. RIE treatment on PEI affected on both of roughness and hydrophilicity increase. Aluminum-chelate adhesion promoter was coated by spinning on silicon wafer. The initial peel strength showed no effect of adhesion promoter treatment, but high temp/high humidity resistance increased remarkably. Al-chelate adhesion promoter did not affect the roughness but increased hydrophilicity.