Electrochemical behaviors of surface modified and MC3T3-El cell cultured Ti-30Ta alloys have been investigated using various electrochemical methods. The Ti alloys containing Ta were melted by using a vacuum furnace and then homogenized for 6 hrs at 1000℃. MC3T3-El cell culture was performed with MC3T3-El mouse osteoblasts for 2 days. The microstructures and corrosion resistance were measured using FE-SEM, XRD, EIS and potentiodynamic test in artificial saliva solution at 36.5±1℃. Ti-Ta alloy showed the martensite structure of α+β phase and micro-structure was changed from lamellar structure to needle-like structure as Ta content increased. Corrosion resistance increased as Ta content increased. Corrosion resistance of cell cultured Ti- Ta alloy increased predominantly in compared with non cell cultured Ti- Ta alloy due to inhibition of the dissolution of metal ion by covered cell. RP value of MC3T3-El cell cultured Ti-40 Ta alloy showed 1.60×10? Ω㎠ which was higher than those of other Ti alloy. Polarization resistance of cell-cultured Ti-Ta alloy increased in compared with non-cell cultured Ti alloy.

목차 (Table of Contents)

Abstract
1. 서론
2. 실험 방법
3. 결과 및 고찰
4. 결론

Abstract
1. 서론
2. 실험 방법
3. 결과 및 고찰
4. 결론
참고문헌

참고문헌 (Reference)

1 M. Niinomi, 243 : 231-, 1998

2 D. Krupa, 22 : 2139-, 2001

3 M. Therin, 2 : 1-, 1991

4 N. R. Van, 22 : 3801-, 1987

5 E. Kobayashi, 54 : 410-, 1985

6 M. F. Semlitsch, 13 : 781-, 1992

7 Y. Okazaki, 9 : 890-, 1996

8 A. K. Shukla, 389 : 144-, 2005

9 D. Kuroda, A 243 : 244-, 2001

10 Y. L. Zhou, A 384 : 92-, 2004

1 M. Niinomi, 243 : 231-, 1998

2 D. Krupa, 22 : 2139-, 2001

3 M. Therin, 2 : 1-, 1991

4 N. R. Van, 22 : 3801-, 1987

5 E. Kobayashi, 54 : 410-, 1985

6 M. F. Semlitsch, 13 : 781-, 1992

7 Y. Okazaki, 9 : 890-, 1996

8 A. K. Shukla, 389 : 144-, 2005

9 D. Kuroda, A 243 : 244-, 2001

10 Y. L. Zhou, A 384 : 92-, 2004

11 Y. L. Zhou, A 371 : 283-, 2004

12 Y. L. Zhou, A 398 : 28-, 2005

13 S. G. Fedotov, Nauka 29-, 1982

14 S. G. Fedotov, Nauka 78-, 1982

15 G. I. Nosova, Nauka 1968

16 E. W. Collings, ASM 1986

17 J. E. Davies, 24 : 1289-, 1990

18 K. Anselme, 21 : 1567-, 2000

19 M. Bigerelle, 23 : 1563-, 2002

20 P. Linez-Bataillon, 19 : 133-, 2002

21 N. Ibris, 52 : 653-, 2002

22 J. E. G. Gonzalez, 471 : 109-, 1999

23 E. Kobayashi, 9 : 567-, 1998

24 R. Boyer, "Titanium Alloys" ASMI 1994

동일학술지(권/호) 다른 논문

MPECVD법에 의한 초경인서트 공구의 c-BN 박막 증착
- 한국표면공학회
- 윤수종(Su-Jong yoon)
- 2008
- KCI등재
Solid Phase Crystallization Kinetics of Amorphous Silicon at High Temperatures
- 한국표면공학회
- Won-Eui Hong
- 2008
- KCI등재
고순도 1,4-솔비탄을 이용한 비이온 솔비탄 모노스테아르산 합성
- 한국표면공학회
- 류화열(Hwa Yeal Yu)
- 2008
- KCI등재
HA/Ti 복합층 코팅한 Ti-30Ta-(3~15)Nb 합금의 전기화학적 특성
- 한국표면공학회
- 정용훈(Yong-hoon Jeong)
- 2008
- KCI등재

동일학술지 더보기

분석정보

View

상세정보조회

Usage

원문다운로드

대출신청

복사신청

EDDS신청

동일 주제 내 활용도 TOP

주제

연도별 연구동향

연도별 활용동향

연관논문

연구자 네트워크맵

공동연구자 (7)

유사연구자 (20) 활용도상위20명

인용정보 인용지수 설명보기

학술지 이력

학술지 이력
연월일	이력구분	이력상세
2026	평가예정	재인증평가 신청대상 (재인증)
2022-01-28	학술지명변경	외국어명 : Journal of The Korean Institute of Surface Engineering -> Journal of Surface Science and Engineering
2020-01-01	평가	등재학술지 유지 (재인증)
2017-01-01	평가	등재학술지 유지 (계속평가)
2013-01-01	평가	등재 1차 FAIL (등재유지)
2010-01-01	평가	등재학술지 유지 (등재유지)
2008-01-01	평가	등재학술지 유지 (등재유지)
2005-01-01	평가	등재학술지 선정 (등재후보2차)
2004-01-01	평가	등재후보 1차 PASS (등재후보1차)
2003-01-01	평가	등재후보학술지 유지 (등재후보1차)
2002-01-01	평가	등재후보 1차 FAIL (등재후보1차)
1999-07-01	평가	등재후보학술지 선정 (신규평가)