High Volume Slag를 사용한 저탄소 콘크리트의 역학 및 내구특성 = Dynamic and Durability Properties of the Low-carbon Concrete using the High Volume Slag

다국어 초록 (Multilingual Abstract)

Blast furnace slag (BFS) have many advantages that are related to effective value improvement on applying to concrete while side effects of blast furnace slag also appear. Thus, research team conducted an experiment with high volume slag to see if the attribute of waste alkali accelerator for mixing rate, mixed use of NaOH and Na2SiO3, and early strength agent for mixing rate for replacement ratio and for the types of the stimulants in order to increase the use of blast furnace slag1s powder. As the result of the experiment, when it comes to compression strength, all of the alkali stimulants have been improved as the replacement rate increases except for sodium hydroxide. Among the alkali stimulants, sodium silicate was high on dynamic elastic modulus and absorption factor. In case of early strength agent,the mix of mixing 1.5% and blast furnace slag 75% have showed high strength enhancement. In event of Waste Alkali accelerator, it has showed different consequences for each experiment.

국문 초록 (Abstract)

고로슬래그는 콘크리트의 적용시 효율적인 가치향상과 관련하는 많은 장점도 있으나, 고로슬래그의 사용량 증대에따른 부작용도 나타나고 있다. 따라서 고로슬래그 미분말의활용성 증대를 위해 High Volume Slag를 자극제 종류별,치환율별, 조강제 혼입율별, NaOH, Na2SiO3 혼합사용시,폐알칼리자극제 혼입율별 특성을 알아보기 위해 실험하였다. 실험결과, 압축강도의 경우 수산화나트륨을 제외한 모든알칼리자극제에서 치환율이 증가함에 따라 강도가 증진되었다. 알칼리자극제 중 규산나트륨이 동탄성계수와 흡수율 등에서 높게 나타났으며, 조강제의 경우 혼입율 1.5%와 고로슬래그 치환율 75%가 높은 강도증진을 나타내었다. 폐알칼리자극제의 경우 모든 실험에서 각기 다른 결과를 나타내었다.

참고문헌 (Reference)

1 궉기홍, "알칼리 활성화 슬래그(AAS) 경화체의 콘크리트 2차 제품 활용에 관한 실험적 연구" 대한건축학회 23 (23): 121-128, 2007

2 박상숙, "알칼리 활성반응을 이용한 플라이 애쉬/슬래그 시멘트 개발(2)- 반응생성물과 미세구조 -" 대한환경공학회 29 (29): 810-819, 2007

3 한천구, "등가재령 방법에 의한 고로슬래그 미분말 다량치환 콘크리트의 응결시간 예측" 대한건축학회 26 (26): 71-78, 2010

4 김무한, "고로슬래그미분말을 대량 활용한 콘크리트의 공학적 특성 및 내구특성에 관한 실험적 연구" 대한건축학회 23 (23): 61-68, 2007

5 An YJ, "The Properties of Alkali Activated Slag Mortarsusing Sodium Silicate with Activator" 26 (26): 26-22, 2006

6 Oh SH, "Study on compressive strength and flowing characteristics of alkali-activated mortar containing blast furnace slag" University of Sungkyunkwan 2011

7 Cheema DS, "Low calcium fly ash geopolymer concrete : a promising sustainable alternative for rigid concrete road furniture, In 25th ARRB Conference" ARRB Group Ltd 10-, 2012

8 Han CG, "Effects of stimulant types on initial strength of concrete replaced by high volume of blast furnace slag powder" 61-64, 2010

9 Chonbuk National University, "Development of Cement Production Technology without Sintering Process by Combination of Inorganic Industrial Wastes for Zero CO2 Emission" Ministry of Environment 32-34, 2007

10 Kim SW, "An Experimental Study on the Durability of High Performance Concrete according to the Replacement ratio of Blast Furnace Slag" 565-568, 2007

11 Won H., "A laboratory study on anti-acid mortar using calcium-aluminate cement and blast-furnace slag with fly-ash" Seoul National University of Science Technology 2010