알칼리 자극제의 종류 및 양생조건이 메타카올린을 이용한 무기결합재 모르타르의 강도발현 특성에 미치는 영향 = Influence of Alkali Activators and Curing Conditions on Strength Development of Inorganic Binder Mortars using Meta-Kaolin

다국어 초록 (Multilingual Abstract)

For the development of high strength inorganic binder mortars containing domestic meta-kaolin, influence of alkali activators and curing conditions on the strength and microstructure of inorganic binder mortars using meta-kaolin (MK-IBM) were investigated. As the results, the considerable improvement of strength was found in MK-IBM added Na2CO3 3% by weight of the binder (meta-kaolin), the compressive strength of this mortar was more than 81 MPa by steam curing at 90℃. The strength of MK-IBM increased significantly by increasing of curing temperature, but the effects of curing temperature were different with the type of alkali activator and the addition rates.

국문 초록 (Abstract)

본 연구에서는 국내산 메타카올린을 이용한 고강도 무기결합재 복합체의 개발을 위한 기초적 연구로서 알칼리 자극제의 종류 및 첨가량, 양생조건 등이 메타카올린 혼입 무기결합재 모르타르의 미세구조 및 강도발현 특성에 미치는 영향을 구명하고자 수행하였다. 시험결과, 탄산나트륨(Na2CO3) 3% 혼입한 메타카올린 혼입 무기결합재 모르타르의 강도발현 특성이 가장 우수하였고 90℃ 증기양생에 의해 압축강도가 약 81MPa까지 증진되었다. 양생온도의 증가는 무기결합재 모르타르의 강도향상 및 치밀한 미세구조 형성에 큰 효과가 있지만, 알칼리 자극제의 종류 및 첨가량에 따라 매우 다르게 나타나 사용시 주의가 필요함을 보여주었다.

참고문헌 (Reference)

1 정석조, "플라이애쉬와 메타카올린을 사용한 무기결합재의 개발" 433-436, 2005

2 궉기홍, "알칼리 활성화 슬래그(AAS) 경화체의 콘크리트 2차 제품 활용에 관한 실험적 연구" 대한건축학회 23 (23): 121-128, 2007

3 이영재, "알칼리 활성화 슬래그 콘크리트의 적용에 관한 실험적 연구" 대한건축학회 23 (23): 99-106, 2007

4 위준우, "알칼리 활성화 반응에 의한 고로슬래그 경량골재 콘크리트의 실험적 연구" 대한건축학회 26 (26): 87-94, 2010

5 이상수, "알칼리 자극제를 사용한 무시멘트계 친환경 무기복합체의 유동특성 및 강도특성 연구" 대한건축학회 26 (26): 67-74, 2010

6 소승영, "메타카올린을 혼입한 RPC의 미세구조와 강도발현 특성" 대한건축학회 27 (27): 147-154, 2011

7 Wang S, "Factors affecting the strength of alkali-activatedslag" 25 (25): 1033-1043, 1994

8 Shi C, "Alkali-activated Cements and Concretes" Taylor & Francis 2006