이산화황 농도에 따른 금속시편의 손상 특성 = Damage Characteristics of Metal Materials According to the SO2 Concentration

다국어 초록 (Multilingual Abstract)

A study has been carried out on metal materials in order to identify the quantitative relation between the concentration and damage characteristics after evaluation of the damage characteristics according to the SO2 concentration. The prepared metal samples, which were categorized according to the material (silver, copper, iron, lead, brass) were exposed to 0.01, 0.12, 1, 10, 100, 1,000, and 5,000ppm of SO2 for 24 hours and the optical, physical, chemical deterioration rates both before and after testing were evaluated. The results showed optical deterioration, a loss of gloss on silver specimen with SO2 100ppm, an increase of color difference on brass, iron, copper and lead specimens with SO2 5,000ppm, as well as physical changes such as an increase of thickness and corrosion rate on iron sample with SO2 5,000ppm. In the case of chemical changes such as an increase sulfate ion (SO4 2-) concentration and decrease of pH on iron and brass specimens were identified. These results suggest that SO2 100ppm caused clear optical deterioration on some metals such as silver and physicochemical and optical deterioration were identified at SO2 5,000ppm regardless of metal type. Also, It was concluded that iron and brass are the most susceptible of the metal specimens to SO2.

국문 초록 (Abstract)

본 연구는 주요 금속문화재 재질 5종(은, 구리, 철, 납, 황동)을 대상으로 이산화황(SO2) 농도에 따른 손상 특성을 분석하여 농도와 손상 특성 간의 정량적인 상관성을 확립하고자 하였다. 금속시편을 대상으 로 가스부식시험기를 이용하여 SO2 0.01, 0.12, 1, 10, 100, 1,000, 5,000ppm 농도로 24시간 노출을 각각 실시한 후 노출 전·후의 광학적·물리적·화학적 손상 변화를 평가하였다. 이 결과, 금속시편의 광 학적 손상변화는 SO2 100ppm에서 은시편의 광택도 감소와 SO2 5,000ppm에서 황동, 철, 구리, 납시 편의 색차 증가가 나타났으며 물리적 손상 변화는 SO2 5,000ppm에서 철시편의 두께, 부식속도 증가가 나타났다. 또한, 화학적 손상 변화는 SO2 5,000ppm에서 철, 황동시편의 황산이온(SO4 2-) 농도 증가, pH 감소가 나타났다. 이를 통해, 금속시편의 광학적 손상 변화는 SO2 100ppm에서 나타나기 시작하였 고 물리적·화학적·광학적 손상 변화는 SO2 5,000ppm에서 모두 나타나는 것으로 확인되었다. 또한, 금속시편 중 철과 황동이 다른 재질에 비해 SO2에 민감한 것을 알 수 있었다.

참고문헌 (Reference)

1 조종수, "金屬文化財의 耐候試驗 槪要" 1 : 1-10, 1980

2 이승은, "용산 새 국립중앙박물관 수장고와 전시실 환경관리 및 측정" 7 : 75-87, 2006

3 정호, "옥외노출소재의 신뢰성 평가기술 및 표준화" 147-154, 2002

4 "소장품 검색"

5 "소장유물검색"

6 김영식, "부식지도 작성을 위한 데이터처리절차 한국부식방식학회규격 - CSSK PD 002-2009"

7 문화체육부, "박물관내 전시 및 수장 공간의 공조환경 기준 연구" 96-102, 1996

8 부경대학교 산학협력단, "동산문화재 보존환경 분석기술 표준화 연구" 국립문화재연구소 469-470, 2008

9 국립환경과학원, "대기환경연보 2010"

10 김현탁, "나라기록관 보존서고의 기록물 보존환경 안정화" 2 : 67-74, 2009

11 Sereda, P. J., "Weather Factors Affecting Corrosion of Metals" American Society for Testing and Materials 7-22, 1974

12 Garry T., "The Museum Environment" Elsevier 136-149, 2005

13 Oesch, S., "The Effect of SO2, NO2, NO and O3 on the Corrosion of Unalloyed Cabon steel and Weathering steel - The Results of Laboratory Exposures" 38 : 1357-1368, 1996

14 Mohamed W. M. H., "Sulfur dioxide, hydrogen sulfide, total reduced sulfur, chlorinated hydrocarbons and photochemical oxidants in southern California museums" 25 : 1497-1505, 1991

15 Lee E. J., "Recent Development on Atmospheric Corrosion of Metals - Investigation of Method and Some Experimental Results -" 22 : 203-209, 1993

16 Pamela B. H., "Pollutants in the Museum Environment" Archetype publications 9-32, 2002

17 기술표준원, "KS L 2405 거울면 광택도 측정 방법"

18 기술표준원, "KS K ISO 3071 텍스타일-수성 추출액의 pH 측정"

19 기술표준원, "KS I 3206 공업용수의 시험 방법"

20 기술표준원, "KS D ISO 8407 금속 및 합금의 부식 - 부식시편에서 부식생성물 제거"

21 기술표준원, "KS D ISO 7384 인공대기에서의 부식 시험- 일반 요구 사항"

22 기술표준원, "KS D ISO 11845 금속 및 합금의 부식 - 부식시험의 일반원리"

23 기술표준원, "KS D ISO 10111 금속 및 무기질 피막 - 단위면적당 질량의 측정 -화학분석 및 무게측정법 총설"

24 기술표준원, "KS D ISO 10062 오염가스의 농도가 매우 낮은인공대기에서의 부식시험"

25 기술표준원, "KS A 0063 색차 표시 방법"

26 Quing Q., "Effects of NaCl and SO2 on the initial atmospheric corrosion of zinc" 2789-2803, 2002

27 Lin C. C., "Correlation between accelerated corrosion tests and atmospheric corrosion tests on steel" 35 : 837-843, 2005

28 Syed, S., "Atmospheric Corrosion of Materials" 11 : 1-24, 2006

29 Environmental Criteria and Assessment office of Research and Development, "A Review of Pollutant Damage to Materials" EPA 5-20, 1980